PA66 Leona™ FR370 ASAHI JAPAN
23
- Unit Price:
- $4764 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- Huangpu port, China
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan East Asia Plastic Co., Ltd.
+86 138****46
1925********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Density | ASTM D792/ISO 1183 | 1.16 | ||
Modeling Shrinkage | ASTM D955 | 0.9-1.6 | % | |
Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 2.3 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | 干 | 旭化成方法 | 0.9-1.6 | % |
MD | 内部方法 | 0.90to1.6 | % | |
Taber Abrasion Resistance | 湿 | ASTM D-1044 | 7 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flexural Modulus | 干(湿) | ASTM D-790 | 3.3(1.3) | GPa |
Elongation at break | 干(湿) | ASTM D-638 | 7(70) | % |
Notched Izod Impact Strength | 干(湿) | ASTM D-256 | 29(58) | J/m |
Flexural Stress | 23°C | ISO178 | 124 | Mpa |
Tensile Strength | 干(湿) | ASTM D-790 | 128(56) | Mpa |
Tensile Strength | ASTMD638 | 83.0 | Mpa | |
Tensile Stress | Yield,23°C | ISO527-2 | 83.0 | Mpa |
Break,23°C | ISO527-2 | 80.0 | Mpa | |
Tensile Strain | Yield,23°C | ISO527-2 | 4.5 | % |
Break,23°C | ISO527-2 | 15 | % | |
Tensile Elongation?(Break) | ASTM D638/ISO 527 | 7 | % | |
Tensile Modulus | 23°C | ISO527-2 | 3600 | Mpa |
Tensile Strength | ASTM D638/ISO 527 | 83.4 | kg/cm²(MPa)[Lb/in²] | |
干(湿) | ASTM D-638 | 83(58) | Mpa | |
Tensile Elongation | Break | ASTMD638 | 7.0 | % |
Rockwell Hardness | 干(湿) | ASTM D-785 | 85(55) | M Scale |
干(湿) | ASTM D-785 | 120(110) | R scale | |
Flexural Modulus | ASTM D790/ISO 178 | 3330 | kg·cm/cm(J/M)ft·lb/in | |
ASTMD790 | 3300 | Mpa | ||
23°C | ISO178 | 3600 | Mpa | |
Flexural Strength | ASTMD790 | 128 | Mpa | |
ASTM D790/ISO 178 | 127 | kg·cm/cm(J/M)ft·lb/in | ||
Charpy impact strength | ASTM D256/ISO 179 | 29 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Linear thermal expansion coefficient | MD | ASTMD696 | 7E-05 | cm/cm/°C |
Flame retardancy | 干 | UL 94 | V-0 | |
Burning Rate | UL94 | V-0 | ||
Deflection Temperature Under Load? | ASTM D648/ISO 75 | 240 | ℃(℉) | |
0.45MPa,Unannealed | ASTMD648 | 240 | °C | |
0.45MPa,Unannealed | ISO75-2/B | 239 | °C | |
1.8MPa,Unannealed | ASTMD648 | 80.0 | °C | |
1.8MPa,Unannealed | ISO75-2/A | 78.0 | °C | |
0.46MPa,干 | ASTM D-648 | 240 | °C | |
1.82MPa,干 | ASTM D-648 | 80 | °C | |
Linear expansion coefficient | ASTM D696/ISO 11359 | 8 | mm/mm.℃ | |
干 | ASTM D-696 | 7 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Surface Resistivity | ASTMD257 | 1E+13 | ohms | |
IEC60093 | 1E+13 | ohms | ||
Volume Resistivity | ASTMD257 | 1E+14 | ohms·cm | |
23°C | IEC60093 | 1E+14 | ohms·cm | |
ASTM D257/IEC 60093 | 10*10 | Ω.cm | ||
Comparative Tracking Index | 3.00mm | IEC60112 | 600 | V |
Dielectric Strength | ASTMD149 | 22 | KV/mm | |
IEC60243-1 | 22 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | ISO179 | 58 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | M-Sale | ASTMD785 | 85 | |
R-Sale | ASTMD785 | 120 | ||
M-Sale | ISO2039-2 | 85 | ||
R-Sale | ISO2039-2 | 120 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 0.75mm | UL94 | V-0 | |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
Oxygen Index | ASTMD2863 | 36 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Moisture Absorption | 湿 | 2.3 | % |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Oxygen Index | 干 | ASTM D-2863 | 36 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Other Prices
Port of Loading | Unit Price |
---|---|
China Main Port | 4701 USD/MT |