PA66 Leona™ FR370 ASAHI JAPAN
220
- Unit Price:
- $4671 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Halogen-free
- Application Areas:Electrical field Electrical components Electronic field switch Connector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.16 | ||
| Molding shrinkage rate | ASTM D955 | 0.9-1.6 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 2.3 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.90to1.6 | % |
| 干 | 旭化成方法 | 0.9-1.6 | % | |
| Wear rate | 湿 | ASTM D-1044 | 7 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 3.3(1.3) | GPa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 7(70) | % |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 29(58) | J/m |
| Bending stress | 23°C | ISO178 | 124 | Mpa |
| Flexural strength | 干(湿) | ASTM D-790 | 128(56) | Mpa |
| Tensile strength | ASTMD638 | 83.0 | Mpa | |
| Tensile stress | Yield,23°C | ISO527-2 | 83.0 | Mpa |
| Break,23°C | ISO527-2 | 80.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2 | 4.5 | % |
| Break,23°C | ISO527-2 | 15 | % | |
| elongation at break | ASTM D638/ISO 527 | 7 | % | |
| Tensile modulus | 23°C | ISO527-2 | 3600 | Mpa |
| tensile strength | ASTM D638/ISO 527 | 83.4 | kg/cm²(MPa)[Lb/in²] | |
| 干(湿) | ASTM D-638 | 83(58) | Mpa | |
| elongation | Break | ASTMD638 | 7.0 | % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(110) | R scale |
| 干(湿) | ASTM D-785 | 85(55) | M Scale | |
| Bending modulus | ASTM D790/ISO 178 | 3330 | kg·cm/cm(J/M)ft·lb/in | |
| ASTMD790 | 3300 | Mpa | ||
| 23°C | ISO178 | 3600 | Mpa | |
| bending strength | ASTMD790 | 128 | Mpa | |
| ASTM D790/ISO 178 | 127 | kg·cm/cm(J/M)ft·lb/in | ||
| Charpy impact strength | ASTM D256/ISO 179 | 29 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTMD696 | 7E-05 | cm/cm/°C |
| Flame retardancy | 干 | UL 94 | V-0 | |
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 240 | ℃（℉） | |
| 0.46MPa,干 | ASTM D-648 | 240 | °C | |
| 1.82MPa,干 | ASTM D-648 | 80 | °C | |
| 0.45MPa,Unannealed | ASTMD648 | 240 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 239 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 80.0 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 78.0 | °C | |
| Linear expansion coefficient | 干 | ASTM D-696 | 7 | |
| ASTM D696/ISO 11359 | 8 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+13 | ohms | |
| IEC60093 | 1E+13 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+14 | ohms·cm | |
| 23°C | IEC60093 | 1E+14 | ohms·cm | |
| ASTM D257/IEC 60093 | 10*10 | Ω.cm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 600 | V |
| Dielectric strength | ASTMD149 | 22 | KV/mm | |
| IEC60243-1 | 22 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 58 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 85 | |
| R-Sale | ASTMD785 | 120 | ||
| M-Sale | ISO2039-2 | 85 | ||
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ASTMD2863 | 36 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 2.3 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen index | 干 | ASTM D-2863 | 36 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.