Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.14 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 2.5 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD2.0mm | ASTMD995 | 1.3 | % |
| Modeling Shrinkage | TD2.0mm | ASTMD995 | 2.0 | % |
| Modeling Shrinkage | 干 | 旭化成方法 | 1.3-2.0 | % |
| Moisture Absorption | (23°C,24hr) | ASTMD570 | 2.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Elongation at break | 干(湿) | ASTM D-638 | 50(250) | % |
| Notched Izod Impact Strength | 干(湿) | ASTM D-256 | 39(147) | J/m |
| Flexural Modulus | 干(湿) | ASTM D-790 | 2.8(1.2) | GPa |
| Taber Abrasion Resistance | 湿 | ASTM D-1044 | 7 | |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 39 | J/m |
| Tensile Strength | 干(湿) | ASTM D-790 | 118(54) | Mpa |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 50 | % |
| Tensile Elongation?(Break) | 23°C | ASTMD638 | 50 | % |
| Tensile Strength | 干(湿) | ASTM D-638 | 79(57) | Mpa |
| Tensile Strength | 23°C | ASTMD638 | 79 | Mpa |
| Rockwell Hardness | 干(湿) | ASTM D-785 | 80(55) | M Scale |
| Rockwell Hardness | 干(湿) | ASTM D-785 | 120(108) | R scale |
| Flexural Modulus | | ASTM D790/ISO 178 | 2790 | kg·cm/cm(J/M)ft·lb/in |
| Flexural Modulus | 23°C | ASTMD790 | 2800 | Mpa |
| Flexural Strength | | ASTM D790/ISO 178 | 118 | kg·cm/cm(J/M)ft·lb/in |
| Flexural Strength | 23°C | ASTMD790 | 118 | Mpa |
| Charpy impact strength | | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | 干 | UL 94 | V-2 | |
| Coefficient of Linear Thermal Expansion | 导热系数 | JISR2618 | 0.2 | W/m/K |
| Coefficient of Linear Thermal Expansion | 比热 | | 1670 | J/kg/°C |
| Burning Rate | | UL94 | v-2 | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 230 | ℃（℉） |
| Deflection Temperature Under Load? | 0.46MPa,干 | ASTM D-648 | 230 | °C |
| Deflection Temperature Under Load? | 1.82MPa,干 | ASTM D-648 | 70 | °C |
| Deflection Temperature Under Load? | 0.45MPaUnannealed | ASTMD648 | 230 | °C |
| Deflection Temperature Under Load? | 1.80MPaUnannealed | ASTMD648 | 70 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 8 | mm/mm.℃ |
| Linear expansion coefficient | 干 | ASTM D-696 | 8 | |
| Thermal Conductivity | 干 | | 0.2 | W/(m.K) |
| Specific Heat | 干 | | 1670 | J/(kg.k) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 相对漏电起痕指数 | ASTMD3638 | 600 | V |
| Insulation strength | | ASTMD149 | 20 | KV/mm |
| Volume Resistivity | | ASTM D257/IEC 60093 | 10-10 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | | ASTMD785 | 80 | M（Scale） |
| Rockwell Hardness | | ASTMD785 | 120 | R |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Fire rating | | UL-94 | 0.40mm | V-2 |
| Fire rating | | UL-94 | 0.71mm | V-2 |
| Fire rating | | UL-94 | 1.50mm | V-2 |
| Fire rating | | UL-94 | 3.00mm | V-2 |
| Fire rating | 氧指数 | ASTM2863 | 26 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 湿 | | 2.5 | % |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | 干 | ASTM D-2863 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.