PA66 Leona™ 1300S ASAHI JAPAN

377

Unit Price:
$3487 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
184.11MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High rigidity Good flexibility
Application Areas:Connector parts Automotive sector Consumer goods sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.14
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	2.5	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD2.0mm	ASTMD995	1.3	%
	Shrinkage rate	TD2.0mm	ASTMD995	2.0	%
	Shrinkage rate	Shrinkage rate	干	旭化成方法	1.3-2.0	%
Water absorption rate	(23°C,24hr)	ASTMD570	2.5	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Fracture elongation rate	干(湿)	ASTM D-638	50(250)	%
Cantilever beam notch impact strength	干(湿)	ASTM D-256	39(147)	J/m
Scratch resistance coefficient	干(湿)	ASTM D-790	2.8(1.2)	GPa
Wear rate	湿	ASTM D-1044	7
Impact strength of cantilever beam gap	23°C	ASTMD256	39	J/m
Flexural strength	干(湿)	ASTM D-790	118(54)	Mpa
elongation at break		ASTM D638/ISO 527	50	%
elongation at break	elongation at break	23°C	ASTMD638	50	%
tensile strength	干(湿)	ASTM D-638	79(57)	Mpa
tensile strength	tensile strength	23°C	ASTMD638	79	Mpa
Rockwell hardness	干(湿)	ASTM D-785	120(108)	R scale
Rockwell hardness	Rockwell hardness	干(湿)	ASTM D-785	80(55)	M Scale
Bending modulus		ASTM D790/ISO 178	2790	kg·cm/cm(J/M)ft·lb/in
Bending modulus	Bending modulus	23°C	ASTMD790	2800	Mpa
bending strength		ASTM D790/ISO 178	118	kg·cm/cm(J/M)ft·lb/in
bending strength	bending strength	23°C	ASTMD790	118	Mpa
Charpy impact strength		ASTM D256/ISO 179	39	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Flame retardancy	干	UL 94	V-2
Coefficient of linear expansion	导热系数	JISR2618	0.2	W/m/K
Coefficient of linear expansion	Coefficient of linear expansion	比热		1670	J/kg/°C
Combustibility (rate)		UL94	v-2
Hot deformation temperature		ASTM D648/ISO 75	230	℃（℉）
	Hot deformation temperature	0.46MPa,干	ASTM D-648	230	°C
		Hot deformation temperature	1.82MPa,干	ASTM D-648	70	°C
			Hot deformation temperature	0.45MPaUnannealed	ASTMD648	230	°C
			Hot deformation temperature	Hot deformation temperature	1.80MPaUnannealed	ASTMD648	70	°C
Linear expansion coefficient	干	ASTM D-696	8
Linear expansion coefficient	Linear expansion coefficient		ASTM D696/ISO 11359	8	mm/mm.℃
Thermal conductivity	干		0.2	W/(m.K)
Specific heat capacity	干		1670	J/(kg.k)

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	相对漏电起痕指数	ASTMD3638	600	V
Insulation strength		ASTMD149	20	KV/mm
Volume resistivity		ASTM D257/IEC 60093	10-10	Ω.cm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness		ASTMD785	80	M（Scale）
Rockwell hardness	Rockwell hardness		ASTMD785	120	R

flammability	Test Condition	Test Method	Test Result	Unit
Fire rating		UL-94	0.40mm	V-2
	Fire rating		UL-94	0.71mm	V-2
		Fire rating		UL-94	1.50mm	V-2
			Fire rating		UL-94	3.00mm	V-2
			Fire rating	Fire rating	氧指数	ASTM2863	26	%

Basic performance	Test Condition	Test Method	Test Result	Unit
Moisture absorption rate	湿		2.5	%

Other performance	Test Condition	Test Method	Test Result	Unit
Oxygen index	干	ASTM D-2863	26	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.