PC Makrolon® RX2430 451118 COVESTRO THAILAND
207
- Unit Price:
- $5462 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 89.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High mobility
- Application Areas:electrical equipment Automotive Applications Lighting installation
- Color:--
- Grade:Medical grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density 2 | ISO 60 | 0.66 | g/cm³ | |
| Melt flow rate | 300°C/1.2 kg | ISO 1133 | 20 | g/10 min |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 19.0 | cm3/10min |
| Shrinkage rate | Across Flow | ISO 2577 | 0.60 到 0.80 | % |
| 流量 | ISO 2577 | 0.60 到 0.80 | % | |
| Across Flow : 280°C, 2.00 mm 3 | ISO 294-4 | 0.65 | % | |
| 流量 : 2.00 mm 3 | ISO 294-4 | 0.60 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2/50 | 67.0 | Mpa |
| Break, 23°C | ISO 527-2/50 | 75.0 | Mpa | |
| Tensile strain | Yield, 23°C | ISO 527-2/50 | 6.1 | % |
| Break, 23°C | ISO 527-2/50 | 130 | % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 | % |
| Bending modulus | 23°C | ISO 178 | 2400 | Mpa |
| Bending stress 4 | 23°C | ISO 178 | 100 | Mpa |
| 3.5% Strain, 23°C | ISO 178 | 74.0 | Mpa | |
| Flexural Strain at Flexural Strength | 23°C | ISO 178 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 134 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 122 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 141 | °C |
| -- | ISO 306/B120 | 142 | °C | |
| Ball Pressure Test | 132°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 1.0E+16 | ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+16 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 | °C | ||
| Drying time - Dry Air Dryer | 4.0 | hr | ||
| Suggested maximum moisture content | < 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 250 到 270 | °C | ||
| Temperature in the middle of the barrel | 270 到 290 | °C | ||
| Temperature at the front of the material cylinder | 285 到 305 | °C | ||
| Spray nozzle temperature | 270 到 305 | °C | ||
| Processing (melt) temperature | 280 到 320 | °C | ||
| Mold temperature | 70 到 110 | °C | ||
| Back pressure | 10.0 到 20.0 | Mpa | ||
| Exhaust hole depth | 0.025 到 0.075 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 6 | -30°C, Complete Break | ISO 179/1eA | 14 | kJ/m² |
| 23°C, Partial Break | ISO 179/1eA | 70 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| 23°C | ISO 179/1eU | 无断裂 | ||
| Suspended wall beam notch impact strength 6 | -30°C, Complete Break | ISO 180/A | 12 | kJ/m² |
| 23°C, Partial Break | ISO 180/A | 60 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 70.0 | J |
| 23°C | ISO 6603-2 | 60.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6200 | N |
| 23°C | ISO 6603-2 | 5300 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO 2039-1 | 118 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.36 mm | UL 94 | V-2 | |
| Flash Ignition Temperature | ASTM D1929 | 480 | °C | |
| Self Ignition Temperature | ASTM D1929 | 550 | °C | |
| ISO 9660 | ISO 7391-PC,M,(,,)-18-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.