PC RX2430 451118 COVESTRO THAILAND
Makrolon®
electrical equipment、Automotive Applications、Lighting installation
Flame retardant、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Apparent density 2
ISO 60
g/cm³
0
Melt flow rate
300°C/1.2 kg
ISO 1133
g/10 min
2
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
1
Shrinkage rate
横向流量
ISO 2577
%
0
Shrinkage rate
流量
ISO 2577
%
0
Shrinkage rate
横向流量 : 280°C, 2.00 mm 3
ISO 294-4
%
0
Shrinkage rate
流量 : 2.00 mm 3
ISO 294-4
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Flexural Strain at Flexural Strength
23°C
ISO 178
%
7
Nominal tensile fracture strain
23°C
ISO 527-2/50
%
>
Tensile modulus
23°C
ISO 527-2/1
Mpa
2
Tensile strain
屈服, 23°C
ISO 527-2/50
%
6
Tensile strain
断裂, 23°C
ISO 527-2/50
%
1
Tensile stress
屈服, 23°C
ISO 527-2/50
Mpa
6
Tensile stress
断裂, 23°C
ISO 527-2/50
Mpa
7
Bending modulus
23°C
ISO 178
Mpa
2
Bending stress 4
23°C
ISO 178
Mpa
1
Bending stress 4
3.5% 应变, 23°C
ISO 178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
thermal conductivity
23°C
ISO 8302
W/m/K
0
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/B
°C
1
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : 23 到 55°C
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : 23 到 55°C
ISO 11359-2
cm/cm/°C
6
Electrical performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Surface resistivity
IEC 60093
ohms
1
Volume resistivity
23°C
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Multi axis Instrumented Peak Impact Force
-30°C
ISO 6603-2
N
6
Multi axis Instrumented Peak Impact Force
23°C
ISO 6603-2
N
5
Multi axis Instrumented Impact Energy
-30°C
ISO 6603-2
J
7
Multi axis Instrumented Impact Energy
23°C
ISO 6603-2
J
6
Impact strength of simply supported beam gap 6
-30°C, 完全断裂
ISO 179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 6
23°C, 局部断裂
ISO 179/1eA
kJ/m²
7
Suspended wall beam notch impact strength 6
-30°C, 完全断裂
ISO 180/A
kJ/m²
1
Suspended wall beam notch impact strength 6
23°C, 局部断裂
ISO 180/A
kJ/m²
6
hardness
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Ball pressure hardness
ISO 2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PC/COVESTRO THAILAND/RX2430 451118
Flash Ignition Temperature
ASTM D1929
°C
4
Self Ignition Temperature
ASTM D1929
°C
5