PC LUX9130T-NAT SABIC INNOVATIVE NANSHA

Unit Price:
$6220 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electronic display Lighting applications
Color:--
Grade:Halogen-free flame retardant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	17.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	内部方法	0.45 到 0.65	%
Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.010	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 2	ASTM D638	2370	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2400	Mpa
Tensile strength	Yield 3	ASTM D638	64.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	64.0	Mpa
		Tensile strength	Break 3	ASTM D638	59.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	50.0	Mpa
elongation	Yield 3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break 3	ASTM D638	72	%
		elongation	elongation	Break	ISO 527-2/50	52	%
Bending modulus	50.0 mm Span 4	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2410	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	98.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 8	ISO 75-2/Be	131	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 8	ISO 75-2/Ae	120	°C
Vicat softening temperature	--	ASTM D15259, ISO 306/B509	137	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	139	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.1E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI Elec		UL 746	115	°C
RTI Imp		UL 746	115	°C

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1.10 GHz	ASTM ES7-83	2.81
Dissipation factor	1.10 GHz	ASTM ES7-83	5.8E-3
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 2

injection	Test Result	Unit
drying temperature	120	°C
drying time	3.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	265 到 290	°C
Temperature in the middle of the barrel	275 到 300	°C
Temperature at the front of the material cylinder	290 到 310	°C
Spray nozzle temperature	280 到 305	°C
Processing (melt) temperature	290 到 310	°C
Mold temperature	70 到 95	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 6	-30°C	ISO 179/1eA	9.0	kJ/m²
Impact strength of simply supported beam gap 6	Impact strength of simply supported beam gap 6	23°C	ISO 179/1eA	9.0	kJ/m²
Simple supported beam without notch impact strength 6	-30°C	ISO 179/1eU	无断裂
Simple supported beam without notch impact strength 6	Simple supported beam without notch impact strength 6	23°C	ISO 179/1eU	无断裂
Non notched cantilever beam impact	-30°C	ASTM D4812	无断裂
	Non notched cantilever beam impact	23°C	ASTM D4812	无断裂
		Non notched cantilever beam impact	-30°C 7	ISO 180/1U	130	kJ/m²
		Non notched cantilever beam impact	Non notched cantilever beam impact	23°C 7	ISO 180/1U	130	kJ/m²
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	55.0	J

optical performance	Test Condition	Test Method	Test Result	Unit
transmissivity	1000 µm	内部方法	> 90.5	%
	transmissivity	2000 µm	内部方法	> 90.0	%
		transmissivity	3000 µm	内部方法	> 89.5	%
		transmissivity	transmissivity	6000 µm	ASTM D1003	> 88.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	6.0 mm	UL 94	5VA
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.