Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX9130T-NAT SABIC INNOVATIVE NANSHA
--
Electronic display、Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
Melt flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
6
elongation
屈服
ISO 527-2/50
%
6
elongation
断裂 3
ASTM D638
%
7
elongation
断裂
ISO 527-2/50
%
5
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Vicat softening temperature
--
ASTM D15259, ISO 306/B509
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
8
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 8
ISO 75-2/Be
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 8
ISO 75-2/Ae
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
Impact strength of simply supported beam gap 6
-30°C
ISO 179/1eA
kJ/m²
9
Impact strength of simply supported beam gap 6
23°C
ISO 179/1eA
kJ/m²
9
Non notched cantilever beam impact
-30°C 7
ISO 180/1U
kJ/m²
1
Non notched cantilever beam impact
23°C 7
ISO 180/1U
kJ/m²
1
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
Hot filament ignition temperature
1.5 mm
IEC 60695-2-13
°C
8
Burning wire flammability index
1.5 mm
IEC 60695-2-12
°C
9
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9130T-NAT
transmissivity
1000 µm
内部方法
%
>
transmissivity
2000 µm
内部方法
%
>
transmissivity
3000 µm
内部方法
%
>
transmissivity
6000 µm
ASTM D1003
%
>