PC LEXAN™ DMX1435 NA90016T SABIC INNOVATIVE US
128
- Unit Price:
- $10115 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 116.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Scratch resistant High temperature resistan high strength
- Application Areas:Wire and cable Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| proportion | ASTM D792 | 1.2 | g/cm³ | |
| ISO 1183 | 1.17 | g/cm³ | ||
| Shrinkage rate | Flow3.2mm | 内部测试方法 | 0.5-0.8 | % |
| Water absorption rate | 24hr | ASTM D570 | 0.08 | % |
| 23℃Equilibrium | ASTM D570 | 0.28 | % | |
| 50RHEquilibrium | ASTM D570 | 0.13 | % | |
| 50RH 24hr | ASTM D570 | 0.04 | % | |
| 23℃Saturation | ISO 62 | 0.27 | % | |
| 23℃ 50RH | ISO 62 | 0.13 | % | |
| Melt index | 300℃ 1.2kg | ASTM D1238 | 14.5 | g/10min |
| 300℃ 1.2kg | ISO 1133 | 13 | cm3/10min | |
| Bi Rong | ASTM D792 | 0.85 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 50mm/min | ASTM D638 | 2900 | Mpa |
| 1.0mm/min | ISO 527 | 2450 | Mpa | |
| tensile strength | Yield50mm/min I型 | ASTM D638 | 80 | Mpa |
| Break50mm/mini型 | ASTM D638 | 65 | Mpa | |
| Yield50mm/min | ISO 527 | 80 | Mpa | |
| 斯裂50mm/min | ISO 527 | 60 | Mpa | |
| elongation | Yield50mm/min iI型 | ASTM D638 | 7 | % |
| Break50mm/min I型 | ASTM D638 | 70 | % | |
| Yield50mm/min | ISO 527 | 7 | % | |
| Break50mm/min | ISO 527 | 40 | % | |
| bending strength | Yield1.3mm/min | ASTM D790 | 120 | Mpa |
| Yield2.0mm/min | ISO 178 | 108 | Mpa | |
| Bending modulus | 1.3mm/min | ASTM D790 | 2600 | Mpa |
| 2.0mm/min | ISO 178 | 2450 | Mpa | |
| Cantilever beam gap impact | 23℃ | ASTM D256 | 30 | J/m |
| -30℃ | ASTM D256 | 30 | J/m | |
| 23°C 3.0mm A型Notched | ISO 180 | 5 | kJ/m² | |
| “-30℃ 3.0mm A型Notched | ISO 180 | 4 | kJ/m² | |
| Cantilever beam without notch impact | 23℃ | ASTM D4812 | NB | J/m |
| 23°C 3.0mm | ISO 180 | NB | kJ/m² | |
| Cantilever beam without defects □ Impact | -30℃ 3.0mm | ISO 180 | 45 | kJ/m² |
| Impact of simply supported beam gap | 23°C3.0mm 1eA型 | ISO 179 | 3 | kJ/m² |
| Impact of simply supported beam gap- | 30℃ 3.0mm 1eA型^ | ISO 179 | 3 | kJ/m² |
| Simple supported beam without notch impact | 23°C 3.0mm | ISO 179 | NB | kJ/m² |
| -30℃ 3.0mm | ISO 179 | 47 | kJ/m² | |
| Tiber wear and tear | CS-17轮1kg | ASTM D1044 | 10 | mg/1000cy |
| Taiberten loss | CS-17轮1kg | 内部测试方法 | 10 | mg/1000cy |
| Erikson scratch depth | 6N | 内部测试方法 | 14 | micrometer |
| Instrument impact | 23℃总能量 | ASTM D3763 | 30 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | Unannealed0.45MPa 3.2mm | ASTM D648 | 133 | °C |
| Unannealed1.8MPa 3.2mm | ASTM D648 | 119 | °C | |
| 0.45MPa 4.0mm | ISO 75 | 131 | °C | |
| 1.8MPa 4.0mm | ISO 75 | 118 | °C | |
| Vicat softening temperature | 50℃/hr 50N | ASTM DI 525 | 139 | °C |
| 50℃/hr 50N | ISO 306 | 138 | °C | |
| 120℃/hr 50N | ISO 306 | 140 | °C | |
| Linear expansion coefficient flow | -40.0~95℃ | ASTM E831 | 0.000070 | cm/cm/℃ |
| Vertical expansion coefficient | -40.0~95℃ | ASTM E831 | 0.000070 | cm/cm/℃ |
| Coefficient of linear expansion | Flow23~80℃ | ISO 11359 | 0.000070 | cm/cm/℃ |
| 垂直23~80℃ | ISO 11359 | 0.000070 | cm/cm/℃ | |
| thermal conductivity | ASTM C177 | 0.2 | w/(m.℃) | |
| ISO 8302 | 0.2 | w/(m.℃) | ||
| Specific heat capacity | ASTM C351 | 1.4 | J/(g.℃) | |
| Ball pressure test | IEC 60695 | 125 | °C | |
| IEC 60695 | 140 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L标尺 | ASTM D785 | 108 | |
| M标尺 | ASTM D785 | 93 | ||
| Pencil hardness | 1.0kg | ASTM D3363 | H | |
| Ball pressure hardness | H358/30 | ISO 2039 | 128 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 2540pm | ASTM DI 003 | 88 | % |
| Haze | 2540Pm | ASTM D1003 | 0.8 | % |
| Refractive index | ASTM D542 | 1.584 | ||
| ISO 489 | 1.584 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.