Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DMX1435 NA90016T SABIC INNOVATIVE US
LEXAN™
Wire and cable、Electronic and electrical、Automotive components
Scratch resistant、High temperature resistan、high strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/DMX1435 NA90016T
Bi Rong
ASTM D792
cm³/g
0
proportion
ASTM D792
g/cm³
1
proportion
ISO 1183
g/cm³
1
Melt index
300℃ 1.2kg
ASTM D1238
g/10min
1
Melt index
300℃ 1.2kg
ISO 1133
cm3/10min
1
Shrinkage rate
流动3.2mm
内部测试方法
%
0
Water absorption rate
24hr
ASTM D570
%
0
Water absorption rate
23℃平衡
ASTM D570
%
0
Water absorption rate
50RH平衡
ASTM D570
%
0
Water absorption rate
50RH 24hr
ASTM D570
%
0
Water absorption rate
23℃饱和
ISO 62
%
0
Water absorption rate
23℃ 50RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/DMX1435 NA90016T
Erikson scratch depth
6N
内部测试方法
micrometer
1
Impact of simply supported beam gap
23°C3.0mm 1eA型
ISO 179
kJ/m²
3
Impact of simply supported beam gap-
30℃ 3.0mm 1eA型^
ISO 179
kJ/m²
3
Simple supported beam without notch impact
23°C 3.0mm
ISO 179
kJ/m²
N
Simple supported beam without notch impact
-30℃ 3.0mm
ISO 179
kJ/m²
4
Tensile modulus
50mm/min
ASTM D638
Mpa
2
Tensile modulus
1.0mm/min
ISO 527
Mpa
2
tensile strength
屈服50mm/min I型
ASTM D638
Mpa
8
tensile strength
断裂50mm/mini型
ASTM D638
Mpa
6
tensile strength
屈服50mm/min
ISO 527
Mpa
8
tensile strength
斯裂50mm/min
ISO 527
Mpa
6
elongation
屈服50mm/min iI型
ASTM D638
%
7
elongation
断裂50mm/min I型
ASTM D638
%
7
elongation
屈服50mm/min
ISO 527
%
7
elongation
断裂50mm/min
ISO 527
%
4
Tiber wear and tear
CS-17轮1kg
ASTM D1044
mg/1000cy
1
Taiberten loss
CS-17轮1kg
内部测试方法
mg/1000cy
1
Bending modulus
1.3mm/min
ASTM D790
Mpa
2
Bending modulus
2.0mm/min
ISO 178
Mpa
2
bending strength
屈服1.3mm/min
ASTM D790
Mpa
1
bending strength
屈服2.0mm/min
ISO 178
Mpa
1
Cantilever beam gap impact
23℃
ASTM D256
J/m
3
Cantilever beam gap impact
-30℃
ASTM D256
J/m
3
Cantilever beam gap impact
23°C 3.0mm A型缺口
ISO 180
kJ/m²
5
Cantilever beam gap impact
“-30℃ 3.0mm A型缺口
ISO 180
kJ/m²
4
Cantilever beam without defects □ Impact
-30℃ 3.0mm
ISO 180
kJ/m²
4
Cantilever beam without notch impact
23℃
ASTM D4812
J/m
N
Cantilever beam without notch impact
23°C 3.0mm
ISO 180
kJ/m²
N
Instrument impact
23℃总能量
ASTM D3763
J
3
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/DMX1435 NA90016T
Specific heat capacity
ASTM C351
J/(g.℃)
1
thermal conductivity
ASTM C177
w/(m.℃)
0
thermal conductivity
ISO 8302
w/(m.℃)
0
Ball pressure test
IEC 60695
°C
1
Ball pressure test
IEC 60695
°C
1
Vertical expansion coefficient
-40.0~95℃
ASTM E831
cm/cm/℃
0
Hot deformation temperature
未退火0.45MPa 3.2mm
ASTM D648
°C
1
Hot deformation temperature
未退火1.8MPa 3.2mm
ASTM D648
°C
1
Hot deformation temperature
0.45MPa 4.0mm
ISO 75
°C
1
Hot deformation temperature
1.8MPa 4.0mm
ISO 75
°C
1
Vicat softening temperature
50℃/hr 50N
ASTM DI 525
°C
1
Vicat softening temperature
50℃/hr 50N
ISO 306
°C
1
Vicat softening temperature
120℃/hr 50N
ISO 306
°C
1
Coefficient of linear expansion
流动23~80℃
ISO 11359
cm/cm/℃
0
Coefficient of linear expansion
垂直23~80℃
ISO 11359
cm/cm/℃
0
Linear expansion coefficient flow
-40.0~95℃
ASTM E831
cm/cm/℃
0
hardness
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/DMX1435 NA90016T
Ball pressure hardness
H358/30
ISO 2039
Mpa
1
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/DMX1435 NA90016T
transmissivity
2540pm
ASTM DI 003
%
8
Haze
2540Pm
ASTM D1003
%
0