Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Molten Volume Flow Rate (MVR) | 190°C/2.16 kg | ISO 1133 | 4.00 | cm3/10min |
| Shrinkage rate | Across Flow | ISO 294-4 | 1.4 | % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.70 | % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.90 | % |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-2 | 8800 | Mpa |
| Tensile stress | Break | ISO 527-2 | 130 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Tensile creep modulus | 1000 hr | ISO 899-1 | 5800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 163 | °C |
| Melting temperature | | ISO 11357-3 | 168 | °C |
| Linear coefficient of thermal expansion - flow | 23 to 55°C | ISO 11359-2 | 4.0E-5 | cm/cm/°C |
| Maximum operating temperature - short cycle operation | | | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 1.0E+14 | ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14 | ohms·cm |
| Dielectric strength | | IEC 60243-1 | 85 | KV/mm |
| Relative permittivity | 1 MHz | IEC 60250 | 4.00 | |
| Dissipation factor | 1 MHz | IEC 60250 | 7.0E-3 | |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 100 | °C |
| drying time | | | 3.0 | hr |
| Suggested maximum moisture content | | | 0.20 | % |
| Hopper temperature | | | 200 | °C |
| Temperature at the rear of the barrel | | | 205 | °C |
| Temperature in the middle of the barrel | | | 205 | °C |
| Temperature at the front of the material cylinder | | | 210 | °C |
| Spray nozzle temperature | | | 210 | °C |
| Processing (melt) temperature | | | 190 到 230 | °C |
| Mold temperature | | | 60 到 120 | °C |
| Residence Time | | | < 10.0 | min |
| Screw Speed | | | < 18 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 60 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H 961/30 | ISO 2039-1 | 190 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB | |
| ISO Type | | ISO6383-1 | POM-K, M-GNR, 02-003, GF25 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.