Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM N2200G53 BASF KOREA
Ultraform®
Automotive Applications
High hardness、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Molten Volume Flow Rate (MVR)
190°C/2.16 kg
ISO 1133
cm3/10min
4
Shrinkage rate
横向流量
ISO 294-4
%
1
Shrinkage rate
流量
ISO 294-4
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Tensile modulus
ISO 527-2
Mpa
8
Tensile creep modulus
1000 hr
ISO 899-1
Mpa
5
Tensile strain
断裂
ISO 527-2
%
3
Tensile stress
断裂
ISO 527-2
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
1
Melting temperature
ISO 11357-3
°C
1
Linear coefficient of thermal expansion - flow
23 到 55°C
ISO 11359-2
cm/cm/°C
4
Electrical performance
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Surface resistivity
IEC 60093
ohms
1
Dielectric strength
IEC 60243-1
KV/mm
8
Leakage Trace Index
解决方案 A
IEC 60112
V
6
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
kJ/m²
5
hardness
Test Condition
Test Method
Unit
POM/BASF KOREA/N2200G53
Ball pressure hardness
H 961/30
ISO 2039-1
Mpa
1