POM TENAC™ 3010 ASAHI JAPAN
248
- Unit Price:
- $4989 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 219MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance high molecular weight high viscosity
- Application Areas:Gear Electrical field Electronic field Industrial applications Household goods
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | MPa | ISO 527-2 | |
| MPa | ASTM D638 | 68.0 | ||
| tensile elongation | Break | % | ASTM D638 | 75 |
| Break | % | ISO 527-2 | ||
| Bending modulus | MPa | ASTM D790 | ||
| bending strength | MPa | ASTM D790 | 98.0 | |
| Taber wear amount | 1000次 | mg | ASTM D1044 | 13.0 |
| Charpy notch impact strength | 23°C | kJ/m² | ISO 179/1eA | |
| IZOD notch impact strength | J/m | ASTM D256 | 108 | |
| tensile strength | ASTM D638/ISO 527 | 68 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 94 | ||
| Bending modulus | ASTM D790/ISO 178 | 2740 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 98 | kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | MPa | ISO 527-2 | 3100 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal distortion temperature | 1.8MPa,Unannealed | °C | ASTM D648 | 133 |
| 0.45MPa,Unannealed | °C | ISO 75-2/B | 163 | |
| 1.8MPa,Unannealed | °C | ISO 75-2/A | 96.0 | |
| Linear coefficient of thermal expansion | flow | cm/cm/°C | ASTM E831 | 0.00010 |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 133 | ℃（℉） | |
| Thermal distortion temperature | 0.45MPa,Unannealed | °C | ASTM D648 | 172 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | g/cm³ | ASTM D792, ISO 1183 | 1.42 | |
| Melt mass flow rate | g/10 min | ASTM D1238 | 2.8 | |
| 190℃/2.16kg | g/10 min | ISO 1133 | 2.8 | |
| Shrinkage rate | flow | % | ASTM D955, ISO 294-4 | 1.8 to 2.2 |
| Across flow | % | ISO 294-4 | 1.8 to 2.2 | |
| Water absorption rate | 24hr | % | ASTM D570 | 0.20 |
| Rockwell hardness | M-Scale | ASTM D785 | 94 | |
| R-Scale | ASTM D785 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.