Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 3010 ASAHI JAPAN
TENAC™
Electrical field、Electronic field、Engine parts、Industrial applications、Household goods
High impact resistance、high molecular weight、high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/3010
density
ASTM D792, ISO 1183
g/cm³
Shrinkage rate
Across flow
ISO 294-4
%
Water absorption rate
24hr
ASTM D570
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/3010
Tensile modulus
ISO 527-2
Mpa
tensile strength
Yield
ISO 527-2
Mpa
tensile strength
ASTM D638
Mpa
6
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
tensile elongation
Break
ASTM D638
%
7
tensile elongation
Break
ISO 527-2
%
Taber wear amount
1000次
ASTM D1044
mg
1
Bending modulus
ASTM D790
Mpa
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ASTM D790
Mpa
Charpy notch impact strength
23°C
ISO 179/1eA
kJ/m²
Impact strength of cantilever beam gap
ASTM D256
J/m
Thermal performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/3010
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Thermal distortion temperature
1.8MPa,未退火
ASTM D648
°C
Thermal distortion temperature
0.45MPa,未退火
ISO 75-2/B
°C
Thermal distortion temperature
1.8MPa,未退火
ISO 75-2/A
°C
Thermal distortion temperature
0.45MPa,未退火
ASTM D648
°C
1
Linear coefficient of thermal expansion
flow
ASTM E831
cm/cm/°C