Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Parts under the hood of a
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
| MD:23°C,2.00mm | ISO294-4 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.90 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 10000 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 195 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ISO178 | 9600 | Mpa |
| Bending stress | 23°C | ISO178 | 270 | Mpa |
| Poisson's Ratio | 23°C | ISO527 | 0.40 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIStr | 0.75mm | UL746 | 115 | °C |
| 1.5mm | UL746 | 120 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 250 | °C | |
| Melting temperature | ISO11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| TD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| RTIElec | 0.75mm | UL746 | 120 | °C |
| 1.5mm | UL746 | 120 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 85.0 | °C |
| 1.5mm | UL746 | 85.0 | °C | |
| 3.0mm | UL746 | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition (HWI) | 0.75mm | UL746 | PLC4 | |
| 1.5mm | UL746 | PLC4 | ||
| 3.0mm | UL746 | PLC4 | ||
| VolumeResistivity | 3.00mm | IEC60093 | 1E+14 | ohms·cm |
| Dielectric strength | 1.00mm | IEC60243 | 24 | KV/mm |
| Arc resistance | 3.00mm | ASTMD495 | PLC5 | |
| Leakage Trace Index | 3.00mm | IEC60112 | 600 | V |
| High arc combustion index (HAI) | 0.75mm | UL746 | PLC0 | |
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 65 | kJ/m² |
| 23°C | ISO179 | 75 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.