PA66 R530 NAT ASCEND USA
--
Parts under the hood of a
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530 NAT
Shrinkage rate
TD:23°C,2.00mm
ISO294-4
%
0
Shrinkage rate
MD:23°C,2.00mm
ISO294-4
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530 NAT
Tensile modulus
23°C
ISO527-2
Mpa
1
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Bending modulus
23°C
ISO178
Mpa
9
Bending stress
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530 NAT
RTIElec
0.75mm
UL746
°C
1
RTIElec
1.5mm
UL746
°C
1
RTIElec
3.0mm
UL746
°C
1
Evolution Calendar intelligent importer
0.75mm
UL746
°C
8
Evolution Calendar intelligent importer
1.5mm
UL746
°C
8
Evolution Calendar intelligent importer
3.0mm
UL746
°C
1
RTIStr
0.75mm
UL746
°C
1
RTIStr
1.5mm
UL746
°C
1
RTIStr
3.0mm
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD：23to55°C,2.00mm
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：23to55°C,2.00mm
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530 NAT
VolumeResistivity
3.00mm
IEC60093
ohms·cm
1
Dielectric strength
1.00mm
IEC60243
KV/mm
2
Leakage Trace Index
3.00mm
IEC60112
V
6
Impact performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/R530 NAT
Impact strength of simply supported beam without notch
-30°C
ISO179
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
7