PA66 LNP™ THERMOCOMP™ RC004SXS-BKNAT SABIC INNOVATIVE US
139
- Unit Price:
- $22261 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 50% RH, | ASTM D 570 | 0.89 | % |
| 23°C / 50 | ISO 62 | 1.2 | % | |
| Longitudinal shrinkage rate (Flow) | flow, 24 h | ASTM D 955 | 0.2~0.4 | % |
| Shrinkage rate (Across Flow) | xflow, 24 | ASTM D 955 | 0.9~2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 50 mm/ | ASTM D638 | 16680 | Mpa |
| 1 mm/m | ISO 527 | 16740 | Mpa | |
| Bending modulus | 1.3 mm/m | ASTM D790 | 13700 | Mpa |
| 2 mm/m | ISO 178 | 12920 | Mpa | |
| bending strength | / | ISO 178 | 331 | Mpa |
| Tensile strength fracture (brk) | Type I, 5 | ASTM D638 | 222 | Mpa |
| 5 mm/mi | ISO 527 | 242 | Mpa | |
| Tensile elongation fracture (brk) | Type I, 5 | ASTM D638 | 2.2 | % |
| 5 mm/ | ISO 527 | 2.5 | % | |
| Bending strength fracture (brk) | 1.3 mm | ASTM D790 | 348 | Mpa |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Izod Notched on Cantilever Beam | 23℃ (73℉) | ASTM D256 | 67 | |
| 23℃ (73℉)80*10*4 | ISO 180/1A | 6 | J/m² | |
| Cantilever beam without notch (Izod Unnotched) | 23℃ (73℉)80*10*4 | ISO 180/1U | 49 | kJ/m² |
| 23℃ (73℉) | ASTM D4812 | 884 | ||
| Instrumented dart impact energy peak at 23 ℃ (73 ℉) | / | ASTM D3763 | 6 | J |
| Multi axis impact | / | ISO 6603 | 2 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.