Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RC004SXS-BKNAT SABIC INNOVATIVE US
LNP™ THERMOCOMP™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RC004SXS-BKNAT
Shrinkage rate (Across Flow)
xflow, 24
ASTM D 955
%
0
Longitudinal shrinkage rate (Flow)
flow, 24 h
ASTM D 955
%
0
Moisture absorption rate
50% RH,
ASTM D 570
%
0
Moisture absorption rate
23°C / 50
ISO 62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RC004SXS-BKNAT
Tensile modulus
50 mm/
ASTM D638
Mpa
1
Tensile modulus
1 mm/m
ISO 527
Mpa
1
Tensile strength fracture (brk)
Type I, 5
ASTM D638
Mpa
2
Tensile strength fracture (brk)
5 mm/mi
ISO 527
Mpa
2
Tensile elongation fracture (brk)
Type I, 5
ASTM D638
%
2
Tensile elongation fracture (brk)
5 mm/
ISO 527
%
2
Bending modulus
1.3 mm/m
ASTM D790
Mpa
1
Bending modulus
2 mm/m
ISO 178
Mpa
1
bending strength
/
ISO 178
Mpa
3
Bending strength fracture (brk)
1.3 mm
ASTM D790
Mpa
3
Impact performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE US/RC004SXS-BKNAT
Multi axis impact
/
ISO 6603
J
2
Izod Notched on Cantilever Beam
23℃ (73℉)80*10*4
ISO 180/1A
J/m²
6
Cantilever beam without notch (Izod Unnotched)
23℃ (73℉)80*10*4
ISO 180/1U
kJ/m²
4
Instrumented dart impact energy peak at 23 ℃ (73 ℉)
/
ASTM D3763
J
6