PA66 Ultramid® A3HG2 BASF GERMANY
130
- Unit Price:
- $6715 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant Insulation performance Glass fiber reinforced
- Application Areas:Electrical components machine Mechanical components Shell
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1200 | ||
| Molding shrinkage rate | ASTM D955 | 0.9 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 80 （cm3/10min 275℃/5kg ) | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 6.6-7.3 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium,50%RH | ASTMD570 | 2.1 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.1 | % | |
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 80.0 | cm3/10min |
| Shrinkage rate | MD：3.18mm | 0.80 | % | |
| Water absorption rate | Saturation | ASTMD570 | 7.0 | % |
| Saturation,23°C | ISO62 | 7.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | 4600 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 4600 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 165 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | 23°C | ISO527-2 | 4600 | Mpa |
| Tensile strength | Break,23°C | ASTMD638 | 100 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 100 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ASTMD790 | 4480 | Mpa |
| 23°C | ISO178 | 4480 | Mpa | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 2.8 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 7 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 210 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| Peak melting temperature | ASTMD3418 | 260 | °C | |
| Melting temperature (DSC) | ISO3146 | 260 | °C | |
| Linear coefficient of thermal expansion | MD | 3.3E-05 | cm/cm/°C | |
| TD | 7.5E-05 | cm/cm/°C | ||
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 210(1.80MPa) | ℃（℉） | |
| melting point | 260 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 1.50mm | ASTMD257 | 1E+13 | ohms·cm |
| Volume resistivity | IEC60093 | 1E+13 | ohms·cm | |
| Dielectric constant | 1MHz | IEC60250 | 3.50 | |
| Dissipation factor | 1MHz | IEC60250 | 0.014 | |
| Leakage Trace Index | IEC60112 | 550 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 30 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.