Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3HG2 BASF GERMANY
Ultramid®
Electrical components、machine、Mechanical components、Shell
Oil resistant、Insulation performance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
Molding shrinkage rate
ASTM D955
%
0
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
8
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
6
physical property
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
Melt volume flow rate
275°C/5.0kg
ISO1133
cm3/10min
8
Water absorption rate
饱和
ASTMD570
%
7
Water absorption rate
饱和,23°C
ISO62
%
7
Water absorption rate
平衡,23°C,50%RH
ISO62
%
2
Water absorption rate
平衡,50%RH
ASTMD570
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
Tensile strength
断裂,23°C
ASTMD638
Mpa
1
Tensile modulus
23°C
ISO527-2
Mpa
4
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
elongation
断裂,23°C
ASTMD638
%
3
Bending modulus
23°C
ASTMD790
Mpa
4
Bending modulus
23°C
ISO178
Mpa
4
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
4
bending strength
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
7
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
2
Thermal performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature (DSC)
ISO3146
°C
2
Peak melting temperature
ASTMD3418
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
VolumeResistivity
1.50mm
ASTMD257
ohms·cm
1
Leakage Trace Index
IEC60112
V
5
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA66/BASF GERMANY/A3HG2
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3