Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.18 | |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：1.00mm3 | % | 0.60到0.90 | |
| Shrinkage rate | MD：3.00mm4 | % | 1.0到1.6 | |
| Water absorption rate | 23°C,24hr | % | 1.1 | -- |
| Water absorption rate | Saturation,23°C | % | 7.5 | -- |
| Flame resistant grade | | UL 94 | 113 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile fracture strength | 23°C | ASTM D-638 | 12 | kg/cm |
| Ezo De Wei Sheng | Unnotched1/2" 23°C | | 5 | kg.cm/cm |
| Tensile and flexural strength | 23°C | ASTM D-638 | 850 | kg/cm |
| Flexural strength | -40°C | ASTM D-790 | 1210 | kg/cm |
| Flexural modulus | -40°C | ASTM D-790 | 34500 | kg/cm |
| Tensile stress | 23°C | MPa | 85.0 | 65.0 |
| Tensile stress | 80°C | MPa | 45.0 | -- |
| Tensile strain | Break,23°C | % | 7.5 | 7.5 |
| Bending modulus | 23°C | MPa | 3500 | 1500 |
| Bending modulus | 80°C | MPa | 1200 | -- |
| Bending stress | -40°C | MPa | 170 | -- |
| Bending stress | 23°C | MPa | 125 | 70.0 |
| Bending stress | 80°C | MPa | 65.0 | -- |
| Taber abraser | 1000Cycles | mg | 9.00到10.0 | -- |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 244 | -- |
| Melting temperature | | °C | 265 | -- |
| heat deflection temperature | 4.6kg/cm | ASTM D-648 | 244 | °C |
| melting point | | 差示扫描测热计DSC法 | 265 | °C |
| melting point | | | 265 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Arc resistance | 1/8" | ASTM D-150 | 127 | |
| Dielectric strength | 1/8" 短时间 | ASTM D-149 | 17 | KV/mm |
| Volume resistivity | | ASTM D-257 | V-0 | Ω.cm |
| IEC conductivity trace index | 导热率温度指表 | UL 746 | 600 | V |
| Volume resistivity | | ohms·cm | 1E+15 | -- |
| Dielectric strength | | kV/mm | 28 | -- |
| Dielectric constant 5 | 23°C,50Hz | | 5.20 | -- |
| Dissipation factor 5 | 23°C,50Hz | | 0.070 | -- |
| Arc resistance 6 | | sec | 127 | -- |
| Compared to the anti leakage trace index | CTI | V | 600 | -- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 140 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Sale,23°C | | 120 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | | V-0 | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | （24hr）23°C | ASTM D-570 | 1.1 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.