Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3004-V0 TORAY JAPAN
Amilan®
OA device、Electrical components、Electrical appliances、Shell
Flame retardant、Halogen-free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
Water absorption rate
23°C,24hr
%
--
1
Water absorption rate
饱和,23°C
%
--
7
Mechanical performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
Tensile fracture strength
23°C
ASTM D-638
kg/cm
1
Tensile and flexural strength
23°C
ASTM D-638
kg/cm
8
Tensile strain
断裂,23°C
%
7.5
7
Tensile stress
23°C
MPa
65.0
8
Tensile stress
80°C
MPa
--
4
Flexural modulus
-40°C
ASTM D-790
kg/cm
3
Flexural strength
-40°C
ASTM D-790
kg/cm
1
Taber abraser
1000Cycles
mg
--
9
Bending modulus
23°C
MPa
1500
3
Bending modulus
80°C
MPa
--
1
Bending stress
-40°C
MPa
--
1
Bending stress
23°C
MPa
70.0
1
Bending stress
80°C
MPa
--
6
Thermal performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
Hot deformation temperature
0.45MPa,未退火
°C
--
2
heat deflection temperature
4.6kg/cm
ASTM D-648
°C
2
melting point
差示扫描测热计DSC法
°C
2
Melting temperature
°C
--
2
Electrical performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
IEC conductivity trace index
导热率温度指表
UL 746
V
6
Dielectric strength
kV/mm
--
2
Dielectric strength
1/8" 短时间
ASTM D-149
KV/mm
1
Arc resistance 6
sec
--
1
Volume resistivity
ohms·cm
--
1
Volume resistivity
ASTM D-257
Ω.cm
V
Compared to the anti leakage trace index
CTI
V
--
6
Impact performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
Impact strength of simply supported beam without notch
-40°C
kJ/m²
无断裂
1
Basic performance
Test Condition
Test Method
Unit
PA66/TORAY JAPAN/CM3004-V0
Water absorption rate
（24小时）23°C
ASTM D-570
%
1