PA66 Leona™ 13G15 ASAHI JAPAN
226
- Unit Price:
- $3136 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Fatigue resistance Creep resistance high strength High rigidity
- Application Areas:Electrical field Electronic field Engine hood parts component Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 | ||
| Molding shrinkage rate | ASTM D955 | 0.7-1.2 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 2.1 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 干 | 旭化成方法 | 0.7/1.2 | % |
| Wear rate | 湿 | ASTM D-1044 | 9 | ×10-6kg/1000times |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural strength | 干(湿) | ASTM D-790 | 167(108) | Mpa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 49(59) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 94(71) | M Scale |
| 干(湿) | ASTM D-785 | 120(-) | R scale | |
| tensile strength | 干(湿) | ASTM D-638 | 108(79) | Mpa |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 4.9(2.5) | GPa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 2.5(8) | % |
| elongation at break | ASTM D638/ISO 527 | 2.5 | % | |
| Bending modulus | ASTM D790/ISO 178 | 4900 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 167 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 107.9 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 49 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 240 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 4 | mm/mm.℃ | |
| 干 | ASTM D-696 | 4 | ×10-5/K | |
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 258 | °C |
| Flame retardancy | 干 | UL 94 | HB | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 240 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTM D495/IEC 60112 | 142 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 10 | Ω.cm |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 2.1 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.