Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 13G15 ASAHI JAPAN
Leona™
Electrical field、Electronic field、Engine hood parts、component、Automotive sector
Fatigue resistance、Creep resistance、high strength、High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G15
Molding shrinkage rate
ASTM D955
%
0
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
2
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G15
Wear rate
湿
ASTM D-1044
×10-6kg/1000times
9
Shrinkage rate
干
旭化成方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G15
elongation at break
ASTM D638/ISO 527
%
2
Fracture elongation rate
干(湿)
ASTM D-638
%
2
Flexural strength
干(湿)
ASTM D-790
Mpa
1
Scratch resistance coefficient
干(湿)
ASTM D-790
GPa
4
tensile strength
干(湿)
ASTM D-638
Mpa
1
Rockwell hardness
干(湿)
ASTM D-785
M Scale
9
Rockwell hardness
干(湿)
ASTM D-785
R scale
1
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
4
bending strength
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
1
Cantilever beam notch impact strength
干(湿)
ASTM D-256
J/m
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G15
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
1.82MPa,干
ASTM D-648
°C
2
Hot deformation temperature
0.46MPa,干
ASTM D-648
°C
2
Linear expansion coefficient
干
ASTM D-696
×10-5/K
4
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
4
Electrical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/13G15
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1