PA6 Durethan® BKV15H1.0 LANXESS WUXI

164

Unit Price:
$4062 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Electronic and electrical Home appliance components Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		ISO60	0.70	g/cm³
Shrinkage rate	TD:280°C,3.00mm2	ISO2577	0.67	%
	Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO294-4	0.21	%
		Shrinkage rate	MD:280°C,3.00mm2	ISO2577	0.34	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,3.00mm3	ISO2577	0.10	%
Water absorption rate	Saturation,23°C	ISO62	7.8	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.6	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break,23°C	ASTMD638	117	Mpa
Tensile stress	Break,23°C	ISO527-2/5	120	Mpa
elongation	Break,23°C	ASTMD638	3.0	%
Tensile strain	Break,23°C	ISO527-2/5	3.0	%
Bending modulus	23°C	ASTMD790	5700	Mpa
Bending modulus 4	23°C	ISO178/A	5700	Mpa
bending strength	23°C	ASTMD790	185	Mpa
Bending stress 4	3.5%Strain	ISO178/A	--	Mpa
	Bending stress 4	23°C	ISO178	185	Mpa
	Bending stress 4	Bending stress 4	FlexuralStrainatFlexuralStrength5(23°C)		4.0	%
Tensile modulus	23°C	ASTMD638	6310	Mpa
Tensile modulus	Tensile modulus	23°C	ISO527-2/1	6300	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	210	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	180	°C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	55.0	°C
Vicat softening temperature	--	ISO306/B50	200	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	200	°C
Melting temperature 5		ISO11357-3	218	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	8E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity	23°C	IEC60093	1E+13	ohms·cm
Dielectric strength	23°C,1.00mm	IEC60243-1	30	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	4.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	3.70
Dissipation factor	23°C,100Hz	IEC60250	8E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	0.018
Leakage Trace Index	SolutionA	IEC60112	375	V

film	Test Condition	Test Method	Test Result	Unit
Membrane puncture strength	--6	ISO6603-2	1.50	J
Membrane puncture strength	Membrane puncture strength	--7	ISO6603-2	2.00	J
Membrane piercing force	--6	ISO6603-2	505	N
Membrane piercing force	Membrane piercing force	--7	ISO6603-2	560	N

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	35	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	40	kJ/m²
Unscented Izod impact strength	-30°C	ISO180/1U	20	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	25	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	190	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Burning wire flammability index	2.0mm	IEC60695-2-12	650	°C
Extreme Oxygen Index 9		ISO4589-2	23	%
BurningBehavior10		ISO3795	passed

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO1874	PA6/66,GHR,14-060,GF15

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.