Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV15H1.0 LANXESS WUXI
Durethan®
Electronic and electrical、Home appliance components、Automotive Applications
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Apparent density
ISO60
g/cm³
0
Shrinkage rate
TD:280°C,3.00mm2
ISO2577
%
0
Shrinkage rate
TD:120°C,2hr,3.00mm3
ISO294-4
%
0
Shrinkage rate
MD:280°C,3.00mm2
ISO2577
%
0
Shrinkage rate
MD:120°C,2hr,3.00mm3
ISO2577
%
0
Water absorption rate
饱和,23°C
ISO62
%
7
Water absorption rate
平衡,23°C,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Tensile strength
断裂,23°C
ASTMD638
Mpa
1
Tensile modulus
23°C
ASTMD638
Mpa
6
Tensile modulus
23°C
ISO527-2/1
Mpa
6
Tensile strain
断裂,23°C
ISO527-2/5
%
3
Tensile stress
断裂,23°C
ISO527-2/5
Mpa
1
elongation
断裂,23°C
ASTMD638
%
3
Bending modulus
23°C
ASTMD790
Mpa
5
Bending modulus 4
23°C
ISO178/A
Mpa
5
bending strength
23°C
ASTMD790
Mpa
1
Bending stress 4
3.5%Strain
ISO178/A
Mpa
-
Bending stress 4
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
5
Melting temperature 5
ISO11357-3
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Vicat softening temperature
--
ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：23to55°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Surface resistivity
IEC60093
ohms
1
Dielectric strength
23°C,1.00mm
IEC60243-1
KV/mm
3
Leakage Trace Index
解决方案A
IEC60112
V
3
Volume resistivity
23°C
IEC60093
ohms·cm
1
film
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Membrane piercing force
--6
ISO6603-2
N
5
Membrane piercing force
--7
ISO6603-2
N
5
Membrane puncture strength
--6
ISO6603-2
J
1
Membrane puncture strength
--7
ISO6603-2
J
2
Impact performance
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
3
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
Unscented Izod impact strength
-30°C
ISO180/1U
kJ/m²
2
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
2
hardness
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Ball pressure hardness
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PA6/LANXESS WUXI/BKV15H1.0
Extreme Oxygen Index 9
ISO4589-2
%
2
Burning wire flammability index
2.0mm
IEC60695-2-12
°C
6