PA6 Ultramid® B30S BASF GERMANY
189
- Unit Price:
- $3683 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Oil resistant
- Application Areas:Thin walled components Plastic accessories Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| proportion | ISO 1183 | 1140 | kg/㎥ | |
| Shrinkage rate | Flow150x105x3mm 270℃ 50MPa模具温 度:80℃ | ISO 2577 | 1.02 | % |
| 垂直150x105x3mm 270°C 50Mpa模具温 度:80℃ | ISO 2577 | 1.16 | % | |
| Flow 150xW5x3mm120°C4hr | ISO 2577 | 0.32 | % | |
| 垂直 150x105x3mm 120°C4hr | ISO 2577 | 0.4 | % | |
| Water absorption rate | 23℃ | ISO 62 | 10 | % |
| 23℃50RHEquilibrium | ISO 62 | 3 | % | |
| Bulk density | ISO 60 | 700 | kg/㎥ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 1.0mm/min | ISO 527 | （3200干态）（1000湿态） | Mpa |
| tensile strength | Yield50mm/min | ISO 527 | （80干态）（40湿态） | Mpa |
| elongation | Yield50mm/min | ISO 527 | （4干态）（20湿态） | % |
| Break50mm/min | ISO 527 | （20干态）（50湿态） | % | |
| Tensile creep modulus | 1hr | ISO 899 | （800湿态） | Mpa |
| 1000hr | ISO 899 | （600湿态） | Mpa | |
| bending strength | 2.0mm/min | ISO 178 | （110干态）（35湿态） | Mpa |
| 3.5%Strain 2.0mm/min | ISO 178 | （95干态）（25湿态） | Mpa | |
| Bending modulus | 2.0mm/min | ISO 178 | （2900干态）（850湿态） | Mpa |
| Bending strain | 2.0mm/min | ISO 178 | （6干态）（8湿态） | % |
| Cantilever beam gap impact | 23℃ | ISO 180 | （10干态）（30湿态） | kJ/m² |
| Cantilever beam without notch impact | 23℃ | ISO 180 | （NB干态）（NB湿态) | kJ/m² |
| -30℃ | ISO 180 | （NB干态）（NB湿态) | kJ/m² | |
| Impact of simply supported beam gap | 23℃ | ISO 179 | （10干态）（20湿态) | kJ/m² |
| -30°C | ISO 179 | （10干态）（10湿态) | kJ/m² | |
| Simple supported beam without notch impact | 23℃ | ISO 179 | （NB干态）（NB湿态) | kJ/m² |
| -30℃ | ISO 179 | （NB干态）（NB湿态) | kJ/m² | |
| Anti puncture | 最大力23℃ | ISO 6603 | 5900 | N |
| 最大力-30℃ | ISO 6603 | 7300 | N | |
| 23℃ | ISO 6603 | 90 | J | |
| -30℃ | ISO 6603 | 85 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa | ISO 75 | 55 | °C |
| 0.45MPa | ISO 75 | 160 | °C | |
| 8.0MPa | ISO 75 | 45 | °C | |
| Vicat softening temperature | 120℃/hr 50N | ISO 306 | 200 | °C |
| 50℃/hr 50N | ISO 306 | 200 | °C | |
| Melting temperature | 10℃/min | ISO 11357 | 222 | °C |
| Coefficient of linear expansion | Flow23~550℃ | ISO 11359 | 0.00010 | cm/cm/℃ |
| 垂直23~55℃ | ISO 11359 | 0.00011 | cm/cm/℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC 60093 | （10000000000000干态）（10000000000湿态） | Ω.m | |
| Surface resistance | IEC 60093 | （100000000000000干态）（10000000000000湿态） | Ω | |
| Insulation strength | 1.0mm | IEC 60243 | （30干态）（30湿态） | KV/mm |
| Dielectric constant | 100Hz | IEC 60250 | （4干态）（15湿态） | |
| 1MHz | IEC 60250 | （3.5干态）（4湿态） | ||
| Number of dissipation zones | 100Hz | IEC 60250 | （0.017干态）（0.2湿态） | |
| 1MHz | IEC 60250 | （0.02干态）（0.12湿态） | ||
| CTI | 溶液A | IEC 60112 | 600 | V |
| M溶液B | IEC 60112 | 600 | V |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO 2039 | （140干态）（50湿态） | n/mm² |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 本色638mm | UL94 | V-2 | |
| 全色1.5mm | UL94 | \A2 | ||
| 全色3.0mm | UL94 | U2 | ||
| 全色6.0mm | UL94 | V-2 | ||
| Relative temperature of heating wire | 2.0mm | IEC 60695 | 750 | °C |
| Extreme Oxygen Index | 方法A | ISO 4589 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.