Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B30S BASF GERMANY
Ultramid®
Thin walled components、Plastic accessories、Shell
High mobility、Oil resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
proportion
ISO 1183
kg/㎥
1
Bulk density
ISO 60
kg/㎥
7
Shrinkage rate
流动150x105x3mm 270℃ 50MPa模具温 度:80℃
ISO 2577
%
1
Shrinkage rate
垂直150x105x3mm 270°C 50Mpa模具温 度:80℃
ISO 2577
%
1
Shrinkage rate
流动 150xW5x3mm120°C4hr
ISO 2577
%
0
Shrinkage rate
垂直 150x105x3mm 120°C4hr
ISO 2577
%
0
Water absorption rate
23℃
ISO 62
%
1
Water absorption rate
23℃50RH平衡
ISO 62
%
3
Mechanical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
Impact of simply supported beam gap
23℃
ISO 179
kJ/m²
（
Impact of simply supported beam gap
-30°C
ISO 179
kJ/m²
（
Simple supported beam without notch impact
23℃
ISO 179
kJ/m²
（
Simple supported beam without notch impact
-30℃
ISO 179
kJ/m²
（
Anti puncture
最大力23℃
ISO 6603
N
5
Anti puncture
最大力-30℃
ISO 6603
N
7
Anti puncture
23℃
ISO 6603
J
9
Anti puncture
-30℃
ISO 6603
J
8
Tensile modulus
1.0mm/min
ISO 527
Mpa
（
tensile strength
屈服50mm/min
ISO 527
Mpa
（
Tensile creep modulus
1hr
ISO 899
Mpa
（
Tensile creep modulus
1000hr
ISO 899
Mpa
（
elongation
屈服50mm/min
ISO 527
%
（
elongation
断裂50mm/min
ISO 527
%
（
Bending modulus
2.0mm/min
ISO 178
Mpa
（
bending strength
2.0mm/min
ISO 178
Mpa
（
bending strength
3.5%应变 2.0mm/min
ISO 178
Mpa
（
Bending strain
2.0mm/min
ISO 178
%
（
Cantilever beam gap impact
23℃
ISO 180
kJ/m²
（
Cantilever beam without notch impact
23℃
ISO 180
kJ/m²
（
Cantilever beam without notch impact
-30℃
ISO 180
kJ/m²
（
Thermal performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
Hot deformation temperature
1.8MPa
ISO 75
°C
5
Hot deformation temperature
0.45MPa
ISO 75
°C
1
Hot deformation temperature
8.0MPa
ISO 75
°C
4
Melting temperature
10℃/min
ISO 11357
°C
2
Vicat softening temperature
120℃/hr 50N
ISO 306
°C
2
Vicat softening temperature
50℃/hr 50N
ISO 306
°C
2
Coefficient of linear expansion
流动23~550℃
ISO 11359
cm/cm/℃
0
Coefficient of linear expansion
垂直23~55℃
ISO 11359
cm/cm/℃
0
Electrical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
CTI
溶液A
IEC 60112
V
6
CTI
M溶液B
IEC 60112
V
6
Surface resistance
IEC 60093
Ω
（
Insulation strength
1.0mm
IEC 60243
KV/mm
（
Volume resistance
IEC 60093
Ω.m
（
hardness
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
Ball pressure hardness
ISO 2039
n/mm²
（
Flame retardant performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B30S
Extreme Oxygen Index
方法A
ISO 4589
%
2
Relative temperature of heating wire
2.0mm
IEC 60695
°C
7