ABS P2H-AT ELIX POLYMERS SPANISH
162
- Unit Price:
- $2333 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 60MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 16% filler by weight
- Application Areas:Application in the automo
- Color:--
- Grade:Anti static level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40to0.60 | % |
| MD | ISO294-4 | 0.40to0.60 | % | |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 37.0 | cm3/10min |
| density | ISO1183 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Tensile stress | 屈服,23°C | ISO527-2/50 | 44.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 2.1 | % |
| 断裂,23°C | ISO527-2/50 | >15 | % | |
| Tensile modulus | 23°C | ISO527-2/1 | 2500 | Mpa |
| Bending modulus | 23°C | ISO178 | 2400 | Mpa |
| bending strength | 23°C | ISO178 | 70.0 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| MD：23到55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,退火 | ISO75-2/B | 97.0 | °C |
| 1.8MPa,退火 | ISO75-2/A | 93.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 98.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Leakage Trace Index | 解决方案A | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 100 | kJ/m² |
| -30°C | ISO179/1eU | 80 | kJ/m² | |
| -30°C | ISO179/1eU | 80 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| -30°C | ISO179/1eA | 7.0 | kJ/m² | |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 16 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 110 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 700 | °C |
| Burning rate | 2.00mm | ISO3795 | 60 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.