Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS P2H-AT ELIX POLYMERS SPANISH
--
Application in the automo
Filler: Glass fiber reinf、16% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
density
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
3
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
TensileCreepModule
1hr
ISO899-1
Mpa
2
Tensile modulus
23°C
ISO527-2/1
Mpa
2
Tensile creep modulus
1000hr
ISO899-1
Mpa
1
Tensile strain
屈服,23°C
ISO527-2/50
%
2
Tensile strain
断裂,23°C
ISO527-2/50
%
>
Tensile stress
屈服,23°C
ISO527-2/50
Mpa
4
Bending modulus
23°C
ISO178
Mpa
2
bending strength
23°C
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
Hot deformation temperature
0.45MPa,退火
ISO75-2/B
°C
9
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
9
Vicat softening temperature
ISO306/B50
°C
9
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
Surface resistivity
IEC60093
ohms
1
Dielectric strength
23°C,1.00mm
IEC60243-1
KV/mm
3
Leakage Trace Index
解决方案A
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
7
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
7
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
hardness
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
Ball pressure hardness
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
ABS/ELIX POLYMERS SPANISH/P2H-AT
Burning rate
2.00mm
ISO3795
mm/min
6
Burning wire flammability index
2.0mm
IEC60695-2-12
°C
7