PA66 Ultramid® A3W BASF MALAYSIA
75
- Unit Price:
- $4740 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant Fast forming cycle High mobility heat-resisting
- Application Areas:wheel Gear Connector bearing
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 8.0 到 9.0 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 2.5 到 3.1 | % | |
| Shrinkage rate | Across Flow | ISO 294-4 | 1.7 | % |
| 流量 | ISO 294-4 | 1.4 | % | |
| Apparent density | 0.70 | g/cm³ | ||
| Stickiness number | 96% H2SO4 | ISO 307 | 150 | cm³/g |
| Molten Volume Flow Rate (MVR) | 275°C/5.0 kg | ISO 1133 | 100 | cm3/10min |
| Mold Shrinkage - Constrained 3 | 0.85 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2/50 | 25 | % | |
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- | Mpa |
| Tensile stress | Yield | ISO 527-2/50 | 85.0 | Mpa |
| Tensile strain | Yield | ISO 527-2/50 | 4.4 | % |
| Tensile modulus | ISO 527-2 | 3000 | Mpa | |
| Bending modulus | ISO 178 | 2900 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 220 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 75.0 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| specific heat | 1700 | J/kg/°C | ||
| thermal conductivity | DIN 52612 | 0.33 | W/m/K | |
| 温度指数 - at 50% loss of tensile strength | -- 5 | IEC 60216 | 147 | °C |
| -- 6 | IEC 60216 | 121 | °C | |
| Linear coefficient of thermal expansion - flow | 23 to 80°C | ISO 11359-2 | 7.0E-5 到 1.0E-4 | cm/cm/°C |
| Maximum operating temperature - short cycle operation | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1 MHz | IEC 60250 | 0.025 | |
| Relative permittivity | 1 MHz | IEC 60250 | 3.20 | |
| Leakage Trace Index | Solution A | IEC 60112 | 500 | V |
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Residence Time | < 10.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| Hopper temperature | 80 | °C | ||
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 290 | °C | ||
| Temperature in the middle of the barrel | 290 | °C | ||
| Temperature at the front of the material cylinder | 290 | °C | ||
| Spray nozzle temperature | 290 | °C | ||
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.15 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Mold temperature | 60 到 80 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | V-2 | |
| Polymer Abbreviation | PA66 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.