Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3W BASF MALAYSIA
Ultramid®
wheel、Gear、Connector、bearing
Oil resistant、Fast forming cycle、High mobility、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/BASF MALAYSIA/A3W
Molten Volume Flow Rate (MVR)
275°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate
横向流量
ISO 294-4
%
1
Shrinkage rate
流量
ISO 294-4
%
1
Water absorption rate
饱和, 23°C
ISO 62
%
8
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
2
Stickiness number
96% H2SO4
ISO 307
cm³/g
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/BASF MALAYSIA/A3W
Nominal tensile fracture strain
ISO 527-2/50
%
2
Tensile modulus
ISO 527-2
Mpa
3
Tensile creep modulus
1000 hr
ISO 899-1
Mpa
-
Tensile strain
屈服
ISO 527-2/50
%
4
Tensile stress
屈服
ISO 527-2/50
Mpa
8
Bending modulus
ISO 178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/BASF MALAYSIA/A3W
thermal conductivity
DIN 52612
W/m/K
0
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/B
°C
2
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
7
Melting temperature
ISO 11357-3
°C
2
温度指数 - at 50% loss of tensile strength
-- 5
IEC 60216
°C
1
温度指数 - at 50% loss of tensile strength
-- 6
IEC 60216
°C
1
Linear coefficient of thermal expansion - flow
23 到 80°C
ISO 11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PA66/BASF MALAYSIA/A3W
Surface resistivity
IEC 60093
ohms
-
Leakage Trace Index
解决方案 A
IEC 60112
V
5
Volume resistivity
IEC 60093
ohms·cm
1