Material Description

Technical Data Sheet

Material Description

Material Properties:high viscosity
Application Areas:Electronic and electrical
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.7	%
	Shrinkage rate	MD	ISO294-4	1.7	%
		Shrinkage rate	-，Across Flow	%	ISO 294-4	1.6
		Shrinkage rate	Shrinkage rate	-，Flow	%	ISO 294-4	1.7
Water absorption rate	Saturation,23°C,2.00mm	ISO62	0.50	%
	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
		Water absorption rate	-，23C/59RH	%	ISO 62	0.2
		Water absorption rate	Water absorption rate	-，Sat/23C	%	ISO 62	0.5
Melt mass flow rate	250°C/2.16kg	ISO1133	10	g/10min
MediumDensity			1.11	g/cm³
Top out temperature			170	°C
SpecificHeatCapacity of Melt			2100	J/kg/°C
ThermalConductivityofMelt			0.21	W/m/K
Density/specific gravity		g/cm	ISO 1183	1.30
Density/specific gravity	Density/specific gravity		ISO1183	1.30	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Yield point tensile stress	23℃	MPa	ISO 527-1, -2	57
Yield point tensile strain	23℃	%	ISO 527-1, -2
Nominal tensile strain at the fracture point	23℃	%	ISO 527-1, -2
Fracture point tensile strain	23 ℃, 50 mm/min	%	ISO 527-1, -2
Nominal tensile fracture strain		ISO527-2	>50	%
Charpy non notched impact strength	-，-30℃, Type 1, Edgewise	KJ/m	ISO 179	No Break
Charpy non notched impact strength	Charpy non notched impact strength	-，23℃, Type 1, Edgewise	KJ/m	ISO 179	No Break
Charpy notch impact strength	-，-30 ℃, Type 1, Edgewise, Notch A	KJ/m	ISO 179
Charpy notch impact strength	Charpy notch impact strength	-，23 ℃, Type 1, Edgewise, Notch A	KJ/m	ISO 179	5.4
Non notched impact strength	23 ℃, Type 1	KJ/m	ISO 180	No Break
Tensile stress	Yield	ISO527-2	57.0	Mpa
Tensile strain	Yield	ISO527-2	4.0	%
Bending stress		ISO178	85.0	Mpa
Gap impact strength	23 ℃, Type 1, Notch A	KJ/m	ISO 180
Tensile creep modulus	-，1h	MPa	ISO 899-1	2600
	Tensile creep modulus	-，1000h	MPa	ISO 899-1	1800
	Tensile creep modulus	Tensile creep modulus	1000hr	ISO899-1	1800	Mpa
Tensile modulus	23℃	MPa	ISO 527-1, -2	2700
Tensile modulus	Tensile modulus		ISO527-2	2600	Mpa
Bending modulus		ISO178	2300	Mpa
bending strength	23℃	MPa	ISO 178	85
TensileCreepModule	1hr	ISO899-1	2300	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ISO306/B50	175	°C
Melting temperature 2		ISO11357-3	224	°C
Hot deformation temperature	-，0.45 Mpa，Unannealed	℃	ISO 75B-1, -2	160
	Hot deformation temperature	-，1.8Mpa，Unannealed	℃	ISO 75A-1, -2
		Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	115	°C
			Hot deformation temperature	0.45MPa,Annealed	ISO75-2/B	180	°C
				Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	50.0	°C
				Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO75-2/A	60.0	°C
Flame retardancy	1.50 mm		UL94	HB
	Flame retardancy	3.00 mm		UL 94	HB
	Flame retardancy	Flame retardancy	0.750 mm		UL 94	HB
Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：55to160°C	ISO11359-2	1.9E-04	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO11359-2	1.2E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	TD：55to160°C	ISO11359-2	2E-04	cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO11359-2	1.1E-04	cm/cm/°C
Melting temperature		℃	ISO 3146	225
Glass transition temperature 2		ISO11357-2	55.0	°C
Linear coefficient of thermal expansion	平行Flow ，23 to 55℃ (73 to 130°F)	cm/cm/℃	ISO 11359-1, -2	0.00013
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂直Flow ，23 to 55℃ (73 to 130°F)	cm/cm/℃	ISO 11359-1, -2	0.00013

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	100Hz	IEC60250	3.60
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.20
Leakage Trace Index		IEC60112	400	V
Dissipation factor	100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.020
Dielectric strength	--	IEC60243-1	26	KV/mm
	Dielectric strength	1.00mm3	IEC60243-1	26	KV/mm
	Dielectric strength	Dielectric strength	2.00mm4	IEC60243-1	15	KV/mm
Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Unscented Izod impact strength	-30°C	ISO180/1U	130	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eA	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	5.0	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO180/1A	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	5.0	kJ/m²

Other performance	Test Condition	Test Method	Test Result	Unit
Extreme Oxygen Index		%	ISO 4589-1, -2	22

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	22	%
FMVSS flammability		FMVSS302	SE

Supplementary Information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	145	µgC/g
Odor		VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.