Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F10 NC010 DuPont, European Union
Crastin®
Electronic and electrical
high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Density/specific gravity
g/cm
1.30
I
Density/specific gravity
ISO1183
g/cm³
1
Melt mass flow rate
250°C/2.16kg
ISO1133
g/10min
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
1
Shrinkage rate
-，Flow
%
1.7
I
Shrinkage rate
-，Across Flow
%
1.6
I
Water absorption rate
-，Sat/23C
%
0.5
I
Water absorption rate
-，23C/59RH
%
0.2
I
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
0
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Charpy non notched impact strength
-，23℃, Type 1, Edgewise
KJ/m
No Break
I
Charpy non notched impact strength
-，-30℃, Type 1, Edgewise
KJ/m
No Break
I
Charpy notch impact strength
-，23 ℃, Type 1, Edgewise, Notch A
KJ/m
5.4
I
TensileCreepModule
1hr
ISO899-1
Mpa
2
Nominal tensile fracture strain
ISO527-2
%
>
Non notched impact strength
23 ℃, Type 1
KJ/m
No Break
I
Tensile modulus
23℃
MPa
2700
I
Tensile modulus
ISO527-2
Mpa
2
Tensile creep modulus
1000hr
ISO899-1
Mpa
1
Tensile creep modulus
-，1000h
MPa
1800
I
Tensile creep modulus
-，1h
MPa
2600
I
Tensile strain
屈服
ISO527-2
%
4
Tensile stress
屈服
ISO527-2
Mpa
5
Yield point tensile stress
23℃
MPa
57
I
Bending modulus
ISO178
Mpa
2
bending strength
23℃
MPa
85
I
Bending stress
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Glass transition temperature 2
ISO11357-2
°C
5
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
0.45MPa,退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
5
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
6
Hot deformation temperature
-，0.45 Mpa，未退火
℃
160
I
Melting temperature
℃
225
I
Melting temperature 2
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
MD：55to160°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
平行流动方向，23 to 55℃ (73 to 130°F)
cm/cm/℃
0.00013
I
Linear coefficient of thermal expansion
垂直流动方向，23 to 55℃ (73 to 130°F)
cm/cm/℃
0.00013
I
Electrical performance
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Surface resistivity
IEC60093
ohms
1
Dielectric strength
--
IEC60243-1
KV/mm
2
Dielectric strength
1.00mm3
IEC60243-1
KV/mm
2
Dielectric strength
2.00mm4
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
4
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
4
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
5
Unscented Izod impact strength
-30°C
ISO180/1U
kJ/m²
1
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
5
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
5
flammability
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Extreme Oxygen Index
ISO4589-2
%
2
Other performance
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
Extreme Oxygen Index
%
22
I
Supplementary Information
Test Condition
Test Method
Unit
PBT/DuPont, European Union/S600F10 NC010
EmissionofOrganicCompounds
VDA277
µgC/g
1