PC/PBT VALOX™ Resin 420SE0-BK1066 SABIC INNOVATIVE NANSHA

197

Unit Price:
$4037 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
63MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:black
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Bi Rong		ASTM D 792	0.62	cm³/g
proportion		ASTM D 792	1.61	—
Shrinkage rate	Across Flow，3.2-4.6mm	SABIC method	0.6-1	%
	Shrinkage rate	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5	%
	Shrinkage rate	Shrinkage rate	Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8	%
Shrinkage rate	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6	%
Shrinkage rate	Shrinkage rate	Flow，3.2 mm	SABIC method	0.5 - 0.7	%
Water absorption rate	24 hours	ASTM D 570	0.06	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Flexural modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400	Mpa
bending strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186	Mpa
Rockwell hardness	R		119	-
Tensile modulus	5 mm/min	ASTM D 638	11500	Mpa
Tensile strength	Yield，类型L，5 mm/min	ASTM D 638	95	Mpa
Tensile strength	Tensile strength	Break，类型L, 5 mm/min	ASTM D 638	95	Mpa
Stretching and elongating	Yield,类型L, 5 mm/min	ASTM D 638	1.2	%
Stretching and elongating	Stretching and elongating	Break，类型L, 5 mm/min	ASTM D 638	1.2	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
CTE (Coefficient of Linear Expansion)	-40℃-4O℃, Flow	ASTM E 831	0.0000252	1/℃
CTE (Coefficient of Linear Expansion)	CTE (Coefficient of Linear Expansion)	60℃-138℃, Flow	ASTM E 831	0.0000252	1/℃
HDT (Heat Deformation Temperature)	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212	°C
	HDT (Heat Deformation Temperature)	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200	°C
		HDT (Heat Deformation Temperature)	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215	°C
		HDT (Heat Deformation Temperature)	HDT (Heat Deformation Temperature)	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.