Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 420SE0-BK1066 SABIC INNOVATIVE NANSHA
VALOX™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/420SE0-BK1066
Bi Rong
ASTM D 792
cm³/g
0
proportion
ASTM D 792
—
1
Shrinkage rate
横向，3.2-4.6mm
SABIC method
%
0
Shrinkage rate
流动, 1.5-3.2 mm
SABIC method
%
0
Shrinkage rate
流动，3.2-4.6 mm
SABIC method
%
0
Shrinkage rate
横向 ,1.5-3.2 mm
SABIC method
%
0
Shrinkage rate
流动，3.2 mm
SABIC method
%
0
Water absorption rate
24 hours
ASTM D 570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/420SE0-BK1066
Tensile strength
屈服，类型L，5 mm/min
ASTM D 638
Mpa
9
Tensile strength
断裂，类型L, 5 mm/min
ASTM D 638
Mpa
9
Tensile modulus
5 mm/min
ASTM D 638
Mpa
1
Stretching and elongating
屈服,类型L, 5 mm/min
ASTM D 638
%
1
Stretching and elongating
断裂，类型L, 5 mm/min
ASTM D 638
%
1
Flexural modulus
1.3 mm/min, 50 mm span
ASTM D 790
Mpa
9
bending strength
断裂,1.3 mm/min, 50 mm span
ASTM D 790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/420SE0-BK1066
CTE (Coefficient of Linear Expansion)
-40℃-4O℃, 流动
ASTM E 831
1/℃
0
CTE (Coefficient of Linear Expansion)
60℃-138℃, 流动
ASTM E 831
1/℃
0
HDT (Heat Deformation Temperature)
0.45 MPa, 3.2 mm, 未退火
ASTM D 648
°C
2
HDT (Heat Deformation Temperature)
1.82 MPa, 3.2mm, 未退火
ASTM D 648
°C
2
HDT (Heat Deformation Temperature)
0.45 MPa, 6.4 mm，未退火
ASTM D 648
°C
2
HDT (Heat Deformation Temperature)
1.82 MPa, 6.4 mm, 未退火
ASTM D 648
°C
2