Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ISO294-4 | 0.50to0.70 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.15 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.32 | % |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 15 | g/10min |
| Density/specific gravity | | ISO1183/B | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber abraser | | ISO9352 | 45 | % |
| Bending modulus 2 | | ISO178 | 2400 | Mpa |
| Bending stress 2 | | ISO178 | 97.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 71.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Tensile strain | Break | ISO527-2/50 | 150 | % |
| Tensile modulus | | ISO527-2/50 | 2300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Annealed | ISO75-2/B | 143 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 124 | °C |
| Hot deformation temperature | 1.8MPa,Annealed | ISO75-2/A | 140 | °C |
| Ball pressure temperature | | IEC60335-1 | >125 | °C |
| Vicat softening temperature | | ISO306/B50 | 148 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | | IEC60243-1 | 17 | KV/mm |
| Relative permittivity | 1MHz | IEC60250 | 3.00 | |
| Relative permittivity | 100Hz | IEC60250 | 3.00 | |
| Compared to the anti leakage trace index | 2.00mm,SolutionA | IEC60112 | 250 | V |
| Dielectric constant | 1MHz | IEC60250 | 3.00 | |
| Dielectric constant | 60Hz | IEC60250 | 3.00 | |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dissipation factor | 50Hz | IEC60250 | 1E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 2E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 25 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 83 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 73 | |
| Rockwell hardness | R-Sale | ISO2039-2 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ISO489 | 1.586 | |
| transmissivity | | ASTMD1003 | 89.0 | % |
| Haze | | ASTMD1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating 3 | 3.0mm | UL94 | HB | |
| UL flame retardant rating 3 | 1.5mm | UL94 | V-2 | |
| Extreme Oxygen Index 3 | | ISO4589-2 | 26 | % |
| Hot filament ignition temperature 3 | 3.0mm | IEC60695-2-13 | 775 | °C |
| Hot filament ignition temperature 3 | 1.0mm | IEC60695-2-13 | 800 | °C |
| Hot filament ignition temperature 3 | 2.0mm | IEC60695-2-13 | 775 | °C |
| GlowWireFlammability Index3 | 1.0mm | IEC60695-2-12 | 900 | °C |
| GlowWireFlammability Index3 | 2.0mm | IEC60695-2-12 | 875 | °C |
| GlowWireFlammability Index3 | 3.0mm | IEC60695-2-12 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.