Density/specific gravity

ISO1183/B

g/cm³

1

Melt mass flow rate

300°C/1.2kg

ISO1133

g/10min

1

Shrinkage rate

MD

ISO294-4

%

0

Water absorption rate

23°C,24hr

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Tensile modulus

ISO527-2/50

Mpa

2

Tensile strain

屈服

ISO527-2/50

%

6

Tensile strain

断裂

ISO527-2/50

%

1

Tensile stress

屈服

ISO527-2/50

Mpa

6

Tensile stress

断裂

ISO527-2/50

Mpa

7

Taber abraser

ISO9352

%

4

Bending modulus 2

ISO178

Mpa

2

Bending stress 2

ISO178

Mpa

9

Ball pressure temperature

IEC60335-1

°C

>

Hot deformation temperature

1.8MPa,退火

ISO75-2/A

°C

1

Hot deformation temperature

0.45MPa,退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Vicat softening temperature

ISO306/B50

°C

1

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

7

Dielectric strength

IEC60243-1

KV/mm

1

Volume resistivity

IEC60093

ohms·cm

>

Compared to the anti leakage trace index

2.00mm,SolutionA

IEC60112

V

2

Charpy Notched Impact Strength

-30°C

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

23°C

ISO179/1eA

kJ/m²

2

Impact strength of cantilever beam gap

23°C

ISO180/A

kJ/m²

8

GlowWireFlammability Index3

1.0mm

IEC60695-2-12

°C

9

GlowWireFlammability Index3

2.0mm

IEC60695-2-12

°C

8

GlowWireFlammability Index3

3.0mm

IEC60695-2-12

°C

8

Extreme Oxygen Index 3

ISO4589-2

%

2

Hot filament ignition temperature 3

3.0mm

IEC60695-2-13

°C

7

Hot filament ignition temperature 3

1.0mm

IEC60695-2-13

°C

8

Hot filament ignition temperature 3

2.0mm

IEC60695-2-13

°C

7

transmissivity

ASTMD1003

%

8

Haze

ASTMD1003

%

1