PA66 A 50H1 SOLVAY SHANGHAI
158
- Unit Price:
- $3838 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.3 | % |
| 流量 | ISO 294-4 | 1.5 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.88 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 2.7 | % | |
| Outdoor applicability | UL 746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 3800 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2/1A | 85.0 | Mpa |
| Break, 23°C | ISO 527-2/1A | 80.0 | Mpa | |
| Tensile strain | Break, 23°C | ISO 527-2 | 12 | % |
| Bending modulus | 23°C | ASTM D790 | 3800 | Mpa |
| 23°C | ISO 178 | 3700 | Mpa | |
| bending strength | 23°C | ASTM D790 | 125 | Mpa |
| 23°C | ISO 178 | 135 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/Bf | 237 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/Af | 85.0 | °C | |
| Melting temperature | ISO 11357-3 | 263 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 3.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 3.0E+15 | ohms·cm | |
| Dielectric strength | 0.800 mm | IEC 60243-1 | 33 | KV/mm |
| 2.00 mm | IEC 60243-1 | 21 | KV/mm | |
| Relative permittivity | IEC 60250 | 3.50 | ||
| Dissipation factor | IEC 60250 | 0.017 | ||
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Temperature at the rear of the barrel | 260 到 270 | °C | ||
| Temperature in the middle of the barrel | 265 到 275 | °C | ||
| Temperature at the front of the material cylinder | 265 到 275 | °C | ||
| Mold temperature | 60 到 80 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 90 | kJ/m² |
| 23°C | ISO 179/1eU | 80 kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-0 | |
| 0.8 mm | UL 94 | V-0 | ||
| 1.6 mm | UL 94 | V-0 | ||
| 3.2 mm | UL 94 | V-0 | ||
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 | °C |
| 1.6 mm | IEC 60695-2-12 | 960 | °C | |
| 3.2 mm | IEC 60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 960 | °C |
| 0.8 mm | IEC 60695-2-13 | 960 | °C | |
| 1.6 mm | IEC 60695-2-13 | 775 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 33 | % | |
| European Railways Certifications | R22 | EN 45545-2 | HL3 | |
| R23 | EN 45545-2 | HL3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.