PA66 A 50H1 SOLVAY SHANGHAI
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Shrinkage rate
横向流量
ISO 294-4
%
1
Shrinkage rate
流量
ISO 294-4
%
1
Water absorption rate
24 hr, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Tensile modulus
23°C
ISO 527-2/1A
Mpa
3
Tensile strain
断裂, 23°C
ISO 527-2
%
1
Tensile stress
屈服, 23°C
ISO 527-2/1A
Mpa
8
Tensile stress
断裂, 23°C
ISO 527-2/1A
Mpa
8
Bending modulus
23°C
ASTM D790
Mpa
3
Bending modulus
23°C
ISO 178
Mpa
3
bending strength
23°C
ASTM D790
Mpa
1
bending strength
23°C
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Hot deformation temperature
0.45 MPa, 未退火
ISO 75-2/Bf
°C
2
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/Af
°C
8
Melting temperature
ISO 11357-3
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Surface resistivity
IEC 60093
ohms
3
Dielectric strength
0.800 mm
IEC 60243-1
KV/mm
3
Dielectric strength
2.00 mm
IEC 60243-1
KV/mm
2
Leakage Trace Index
解决方案 A
IEC 60112
V
6
Volume resistivity
IEC 60093
ohms·cm
3
Impact performance
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
kJ/m²
9
flammability
Test Condition
Test Method
Unit
PA66/SOLVAY SHANGHAI/A 50H1
Extreme Oxygen Index
ISO 4589-2
%
3
Hot filament ignition temperature
0.40 mm
IEC 60695-2-13
°C
9
Hot filament ignition temperature
0.8 mm
IEC 60695-2-13
°C
9
Hot filament ignition temperature
1.6 mm
IEC 60695-2-13
°C
7
Burning wire flammability index
0.8 mm
IEC 60695-2-12
°C
9
Burning wire flammability index
1.6 mm
IEC 60695-2-12
°C
9
Burning wire flammability index
3.2 mm
IEC 60695-2-12
°C
9