PP DOWLEX™ 2035G STYRON US
120
- Unit Price:
- $1528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 6.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile yield strength (TD) | 23um，Cast Film | ASTM D-882 | 7 | Mpa |
| Tensile yield strength (MD) | 23um，Cast Film | ASTM D-882 | 7 | Mpa |
| Tensile fracture strength (TD) | 23um，Cast Film | ASTM D-882 | 20 | Mpa |
| Tensile strength at break (MD) | 23um，Cast Film | ASTM D-882 | 26 | Mpa |
| Tensile elongation at break (TD) | 23um，Cast Film | ASTM D-882 | 690 | % |
| Tensile elongation at break (MD) | 23um，Cast Film | ASTM D-882 | 520 | % |
| Falling hammer impact | 23um，Cast Film | ASTM D-1709A | 120 | g |
| Elmendorf Tear Strength (MD) | 23um，Cast Film | ASTM D-1922 | 250 | g |
| Elmendorf Tear Strength (TD) | 23um，Cast Film | ASTM D-1922 | 490 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ISO 306/A | 97 | °C | |
| Vicat softening temperature | ISO306/A | 97.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 23 | µm | ||
| Tensile strength 2 | MD:Yield,23μm,挤塑薄膜 | ASTMD882 | 7.00 | Mpa |
| TD:Yield,23μm,挤塑薄膜 | ASTMD882 | 7.00 | Mpa | |
| MD:Break,23μm,挤塑薄膜 | ASTMD882 | 26.0 | Mpa | |
| TD:Break,23μm,挤塑薄膜 | ASTMD882 | 20.0 | Mpa | |
| Elongation rate 2 | MD:Break,23μm,挤塑薄膜 | ASTMD882 | 520 | % |
| TD:Break,23μm,挤塑薄膜 | ASTMD882 | 690 | % | |
| Falling hammer impact 2 | 23µm,铸造薄膜 | ASTMD1709A | 120 | g |
| Elmondov tear strength 2 | MD:23µm,铸造薄膜 | ASTMD1922 | 250 | g |
| TD:23µm,铸造薄膜 | ASTMD1922 | 490 | g | |
| Film tensile performance - load on pallet 3 | ASTMD4649 | 13000 | g | |
| Film tensile performance - improves tear strength - @ maximum tensile rate 3 | ASTMD4649 | 47 | % | |
| Film tensile performance - maximum elongation of 3 | ASTMD4649 | 340 | % |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 220-280 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 20°，23um，Cast Film | ASTM D-2457 | 148 | |
| Haze | 23um，Cast Film | ASTM D-1003 | 0.7 | % |
| Glossiness 2 | 20°,23.0µm,铸造薄膜 | ASTMD2457 | 148 | |
| Haze 2 | 23.0µm,铸造薄膜 | ASTMD1003 | 0.70 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D-792 | 0.919 | g/m3 | |
| Melt flow rate | 190℃/2.16kg | ISO 1133 | 6 | g/10min |
| film thickness | 23 | um |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.