Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 2035G STYRON US
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PP/STYRON US/2035G
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
6
Mechanical performance
Test Condition
Test Method
Unit
PP/STYRON US/2035G
Elmendorf Tear Strength (MD)
23um，Cast Film
ASTM D-1922
g
2
Tensile strength at break (MD)
23um，Cast Film
ASTM D-882
Mpa
2
Tensile fracture strength (TD)
23um，Cast Film
ASTM D-882
Mpa
2
Tensile elongation at break (MD)
23um，Cast Film
ASTM D-882
%
5
Tensile elongation at break (TD)
23um，Cast Film
ASTM D-882
%
6
Tensile yield strength (MD)
23um，Cast Film
ASTM D-882
Mpa
7
Tensile yield strength (TD)
23um，Cast Film
ASTM D-882
Mpa
7
Falling hammer impact
23um，Cast Film
ASTM D-1709A
g
1
Thermal performance
Test Condition
Test Method
Unit
PP/STYRON US/2035G
vicat softening point
ISO 306/A
°C
9
Vicat softening temperature
ISO306/A
°C
9
film
Test Condition
Test Method
Unit
PP/STYRON US/2035G
Elmondov tear strength 2
TD:23µm,铸造薄膜
ASTMD1922
g
4
Elmondov tear strength 2
MD:23µm,铸造薄膜
ASTMD1922
g
2
Film tensile performance - load on pallet 3
ASTMD4649
g
1
Film tensile performance - improves tear strength - @ maximum tensile rate 3
ASTMD4649
%
4
Film tensile performance - maximum elongation of 3
ASTMD4649
%
3
Tensile strength 2
MD:屈服,23µm,挤塑薄膜
ASTMD882
Mpa
7
Tensile strength 2
TD:屈服,23µm,挤塑薄膜
ASTMD882
Mpa
7
Tensile strength 2
MD:断裂,23µm,挤塑薄膜
ASTMD882
Mpa
2
Tensile strength 2
TD:断裂,23µm,挤塑薄膜
ASTMD882
Mpa
2
Falling hammer impact 2
23µm,铸造薄膜
ASTMD1709A
g
1
Elongation rate 2
MD:断裂,23µm,挤塑薄膜
ASTMD882
%
5
Elongation rate 2
TD:断裂,23µm,挤塑薄膜
ASTMD882
%
6
optical performance
Test Condition
Test Method
Unit
PP/STYRON US/2035G
Haze
23um，Cast Film
ASTM D-1003
%
0
Haze 2
23.0µm,铸造薄膜
ASTMD1003
%
0
Basic performance
Test Condition
Test Method
Unit
PP/STYRON US/2035G
density
ASTM D-792
g/m3
0
Melt flow rate
190℃/2.16kg
ISO 1133
g/10min
6