| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/1A/1 | 3100 | Mpa |
| Tensile stress | Yield | ISO527-2/1A/50 | 51.0 | Mpa |
| Tensile strain | Yield | ISO527-2/1A/50 | 3.1 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/Bf | 96.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/Af | 78.0 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 184 | °C |
| Vicat softening temperature | -- | ISO306/B50 | 110 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 75 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H358/10 | ISO2039-1 | 101 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate | | ISO3795 | 30 | mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 675 | °C |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 675 | °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 700 | °C |
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 700 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.