Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA/PA M/MW NC100 A SCHULMAN USA
SCHULABLEND®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
6
Mechanical performance
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Tensile modulus
ISO527-2/1A/1
Mpa
3
Tensile strain
屈服
ISO527-2/1A/50
%
3
Tensile stress
屈服
ISO527-2/1A/50
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Hot deformation temperature
0.45MPa,未退火
ISO75-2/Bf
°C
9
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
7
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Impact performance
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
7
hardness
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Ball pressure hardness
H358/10
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
ASA/PA/A SCHULMAN USA/M/MW NC100
Burning rate
ISO3795
mm/min
3
Hot filament ignition temperature
1.5mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
7
Burning wire flammability index
1.5mm
IEC60695-2-12
°C
6
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
6