EAA PRIMACOR™ 1430 STYRON US
234
- Unit Price:
- $3494 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | g/cm³ | ASTM D-792 | 0.93 | |
| g/cm³ | ISO 1183 | 0.93 | ||
| ASTMD792,ISO1183 | 0.930 | g/cm³ | ||
| Melt mass flow rate 2 | 190°C/2.16kg | ASTMD1238,ISO1133 | 5.0 | g/10min |
| Content of comonomer 3 | 内部方法 | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,Compression Molded4 | ASTMD638 | 7.67 | Mpa |
| Yield,Compression Molded | ISO527-2/508 | 7.67 | Mpa | |
| Break,Compression Molded4 | ASTMD638 | 19.5 | Mpa | |
| Break,Compression Molded | ISO527-2/508 | 19.5 | Mpa | |
| elongation | Break,Compression Molded4 | ASTMD638 | 580 | % |
| Break,Compression Molded | ISO527-2/508 | 580 | % | |
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | 7.67 |
| Compression Molded | MPa | ISO 527-2/508 | 7.67 | |
| Tensile fracture strength | Compression Molded | MPa | ASTM D-638 | 19.5 |
| Compression Molded | MPa | ISO 527-2/508 | 19.5 | |
| Tensile strain at break | Compression Molded | % | ASTM D-638 | 580 |
| Compression Molded | % | ISO 527-2/508 | 580 | |
| Film thickness - Tested | um | 50.8 | ||
| Tensile yield strength (MD) | 50.8um | MPa | ASTM D-882 | 10.4 |
| Tensile yield strength (TD) | 50.8um | MPa | ASTM D-882 | 10.2 |
| Tensile yield strength (MD) | 50.8um | MPa | ISO 527-3 | 10.4 |
| Tensile yield strength (TD) | 50.8um | MPa | ISO 527-3 | 10.2 |
| Tensile fracture strength (TD) | 50.8um | MPa | ASTM D-882 | 31.0 |
| Tensile strength at break (MD) | 50.8um | MPa | ASTM D-882 | 30.6 |
| Tensile fracture strength (TD) | 50.8um | MPa | ISO 527-3 | 31 |
| Tensile strength at break (MD) | 50.8um | MPa | ISO 527-3 | 30.6 |
| Tensile elongation at break (MD) | 50.8um | % | ASTM D-882 | 420 |
| Tensile elongation at break (TD) | 50.8um | % | ASTM D-882 | 470 |
| 50.8um | % | ISO 527-3 | 470 | |
| Tensile elongation at break (MD) | 50.8um | % | ISO 527-3 | 420 |
| Elmendorf Tear Strength (MD) | 50.8um | g | ASTM D-1922 | 470 |
| Elmendorf Tear Strength (TD) | 50.8um | g | ASTM D-1922 | 730 |
| Elmendorf Tear Strength (MD) | 50.8um | N | ISO 6383-2 | 2100 |
| Elmendorf Tear Strength (TD) | 50.8um | N | ISO 6383-2 | 3300 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ℃ | ASTM D-1525 | 76.1 | |
| ℃ | ISO 306 | 76.1 | ||
| Melting temperature | ℃ | Internal Method | ||
| Vicat softening temperature | ASTMD1525,ISO306 | 76.1 | °C | |
| Melting temperature (DSC) | 内部方法 | 96.1 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | MD:Yield,51μm | ASTMD882 | 10.4 | Mpa |
| TD:Yield,51μm | ASTMD882 | 10.2 | Mpa | |
| MD:Yield,51μm | ISO527-3 | 10.4 | Mpa | |
| TD:Yield,51μm | ISO527-3 | 10.2 | Mpa | |
| MD:Break,51μm | ASTMD882,ISO527-3 | 30.6 | Mpa | |
| TD:Break,51μm | ASTMD882,ISO527-3 | 31.0 | Mpa | |
| elongation | MD:Break,51μm | ASTMD882,ISO527-3 | 420 | % |
| TD:Break,51μm | ASTMD882,ISO527-3 | 470 | % | |
| Elmondov tear strength 5 | MD:51µm | ASTMD1922 | 470 | g |
| TD:51µm | ASTMD1922 | 730 | g | |
| MD:51µm | ISO6383-2 | 2100 | N | |
| TD:51µm | ISO6383-2 | 3300 | N |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | 74 | |
| Haze | 50.8um | % | ISO 14782 | |
| 50.8um | % | ASTM D-1003 | ||
| Melt Temperature | ℃ | 196 | ||
| gloss | 45°,50.8µm | ASTMD2457 | 74 | |
| Haze | 50.8µm | ASTMD1003 | 4.0 | % |
| 50.8µm | ISO14782 | 4.0 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 190℃/2.16kg | g/10min | ASTM D-1238 | |
| 190℃/2.16kg | g/10min | ISO 1133 | ||
| Monomer content | % | Internal Method |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.