Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EAA 1430 STYRON US
PRIMACOR™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
EAA/STYRON US/1430
Content of comonomer 3
内部方法
%
9
Density/specific gravity
ASTMD792,ISO1183
g/cm³
0
Density/specific gravity
g/cm³
0.93
A
Density/specific gravity
g/cm³
0.93
I
Melt mass flow rate 2
190°C/2.16kg
ASTMD1238,ISO1133
g/10min
5
Mechanical performance
Test Condition
Test Method
Unit
EAA/STYRON US/1430
Elmendorf Tear Strength (MD)
50.8um
g
470
A
Elmendorf Tear Strength (MD)
50.8um
N
2100
I
Elmendorf Tear Strength (TD)
50.8um
N
3300
I
Elmendorf Tear Strength (TD)
50.8um
g
730
A
Film thickness - Tested
um
50.8
Tensile strength
屈服,模压成型4
ASTMD638
Mpa
7
Tensile strength
屈服,模压成型
ISO527-2/508
Mpa
7
Tensile strength
断裂,模压成型4
ASTMD638
Mpa
1
Tensile strength
断裂,模压成型
ISO527-2/508
Mpa
1
Tensile fracture strength
Compression Molded
MPa
19.5
A
Tensile fracture strength
Compression Molded
MPa
19.5
I
Tensile strength at break (MD)
50.8um
MPa
30.6
I
Tensile strength at break (MD)
50.8um
MPa
30.6
A
Tensile fracture strength (TD)
50.8um
MPa
31
I
Tensile fracture strength (TD)
50.8um
MPa
31.0
A
Tensile strain at break
Compression Molded
%
580
A
Tensile strain at break
Compression Molded
%
580
I
Tensile elongation at break (MD)
50.8um
%
420
A
Tensile elongation at break (MD)
50.8um
%
420
I
Tensile elongation at break (TD)
50.8um
%
470
A
Tensile elongation at break (TD)
50.8um
%
470
I
Tensile yield strength
Compression Molded
MPa
7.67
A
Tensile yield strength
Compression Molded
MPa
7.67
I
Tensile yield strength (MD)
50.8um
MPa
10.4
A
Tensile yield strength (MD)
50.8um
MPa
10.4
I
Tensile yield strength (TD)
50.8um
MPa
10.2
I
Tensile yield strength (TD)
50.8um
MPa
10.2
A
elongation
断裂,模压成型4
ASTMD638
%
5
elongation
断裂,模压成型
ISO527-2/508
%
5
Thermal performance
Test Condition
Test Method
Unit
EAA/STYRON US/1430
Melting temperature (DSC)
内部方法
°C
9
vicat softening point
℃
76.1
A
vicat softening point
℃
76.1
I
Vicat softening temperature
ASTMD1525,ISO306
°C
7
film
Test Condition
Test Method
Unit
EAA/STYRON US/1430
Elmondov tear strength 5
MD:51µm
ASTMD1922
g
4
Elmondov tear strength 5
TD:51µm
ASTMD1922
g
7
Elmondov tear strength 5
MD:51µm
ISO6383-2
N
2
Elmondov tear strength 5
TD:51µm
ISO6383-2
N
3
Tensile strength
MD:屈服,51µm
ASTMD882
Mpa
1
Tensile strength
TD:屈服,51µm
ASTMD882
Mpa
1
Tensile strength
MD:屈服,51µm
ISO527-3
Mpa
1
Tensile strength
TD:屈服,51µm
ISO527-3
Mpa
1
Tensile strength
MD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
Tensile strength
TD:断裂,51µm
ASTMD882,ISO527-3
Mpa
3
elongation
MD:断裂,51µm
ASTMD882,ISO527-3
%
4
elongation
TD:断裂,51µm
ASTMD882,ISO527-3
%
4
optical performance
Test Condition
Test Method
Unit
EAA/STYRON US/1430
Melt Temperature
℃
196
Haze
50.8µm
ASTMD1003
%
4
Haze
50.8µm
ISO14782
%
4