PC/PBT Makroblend® UT6005 901510 COVESTRO GERMANY
118
- Unit Price:
- $3140 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc Creep resistance Resistance to stress crac
- Application Areas:electrical equipment electronic product Communication Application transport
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD2 | ISO2577 | 0.70to0.90 | % |
| TD:90°C,1hr | ISO2577 | 0.10to0.20 | % | |
| MD2 | ISO2577 | 0.70to0.90 | % | |
| MD:90°C,1hr | ISO2577 | 0.10to0.20 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Apparent density | ISO60 | 0.65 | g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 18.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 3 | 23°C | ISO178 | 2150 | Mpa |
| Bending stress 3 | 23°C | ISO178 | 80.0 | Mpa |
| 3.5%Strain,23°C | ISO178 | 70.0 | Mpa | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Tensile stress | Yield,23°C | ISO527-2/50 | 60.0 | Mpa |
| Break,23°C | ISO527-2/50 | 50.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 5.0 | % |
| Tensile modulus | 23°C | ISO527-2/1 | 2200 | Mpa |
| Bending strain 4 | 23°C | ISO178 | 6.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ThermalConductivity5 | 23°C | ISO8302 | 0.20 | W/m/K |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 110 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 85.0 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Vicat softening temperature | ISO306/B120 | 126 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 23°C,100Hz | IEC60250 | 7E-04 | |
| 23°C,1MHz | IEC60250 | 4.5E-03 | ||
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 30 | KV/mm |
| Surface resistivity | IEC60093 | >1.0E+17 | ohms | |
| Volume resistivity | 23°C | IEC60093 | >1.0E+17 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | -30°C | ISO180 | NoBreak | |
| 23°C | ISO180 | NoBreak | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 58.0 | J |
| 23°C | ISO6603-2 | 47.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 5000 | N |
| 23°C | ISO6603-2 | 3800 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 108 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.6mm,BayerTest | UL94 | HB | |
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 750 | °C |
| Extreme Oxygen Index 6 | ISO4589-2 | 21 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.