Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT UT6005 901510 COVESTRO GERMANY
Makroblend®
electrical equipment、electronic product、Communication Application、transport
Low temperature resistanc、Creep resistance、Resistance to stress crac
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Apparent density
ISO60
g/cm³
0
Melt volume flow rate
260°C/5.0kg
ISO1133
cm3/10min
1
Shrinkage rate
TD2
ISO2577
%
0
Shrinkage rate
TD:90°C,1hr
ISO2577
%
0
Shrinkage rate
MD2
ISO2577
%
0
Shrinkage rate
MD:90°C,1hr
ISO2577
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Nominal tensile fracture strain
23°C
ISO527-2/50
%
>
Tensile modulus
23°C
ISO527-2/1
Mpa
2
Tensile strain
屈服,23°C
ISO527-2/50
%
5
Tensile stress
屈服,23°C
ISO527-2/50
Mpa
6
Tensile stress
断裂,23°C
ISO527-2/50
Mpa
5
Bending modulus 3
23°C
ISO178
Mpa
2
Bending strain 4
23°C
ISO178
%
6
Bending stress 3
23°C
ISO178
Mpa
8
Bending stress 3
3.5%Strain,23°C
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
ThermalConductivity5
23°C
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
8
Vicat softening temperature
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：23to55°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Surface resistivity
IEC60093
ohms
>
Dielectric strength
23°C,1.00mm
IEC60243-1
KV/mm
3
Leakage Trace Index
解决方案B
IEC60112
V
1
Leakage Trace Index
解决方案A
IEC60112
V
6
Volume resistivity
23°C
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Multi axis Instrumented Peak Impact Force
-30°C
ISO6603-2
N
5
Multi axis Instrumented Peak Impact Force
23°C
ISO6603-2
N
3
Multi axis Instrumented Impact Energy
-30°C
ISO6603-2
J
5
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
4
hardness
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Ball pressure hardness
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PC/PBT/COVESTRO GERMANY/UT6005 901510
Extreme Oxygen Index 6
ISO4589-2
%
2
Burning wire flammability index
2.0mm
IEC60695-2-12
°C
7