PPA AMODEL® A-4133L BK324 SOLVAY USA

229

Unit Price:
$7991 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
48MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance Low moisture absorption Filler: Glass fiber reinf 33% filler by weight
Application Areas:Lawn and garden equipment Electrical/Electronic App Valves/valve components Industrial components Industrial applications Thick wall accessories (c Machine/mechanical compon Metal substitution Connector Parts under the hood of a Vehicle electronics Application in the automo Phone currency Shell
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.50	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	1.0	%
Water absorption rate	24hr	ASTMD570	0.29	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	11700	Mpa
Tensile strain	Break,23°C	ISO527-2	2.6	%
	Tensile strain	Break,24°C	ISO527-2	4.3	%
		Tensile strain	Break,150°C	ISO527-2	6.6	%
		Tensile strain	Tensile strain	Break,175°C	ISO527-2	6.6	%
Bending modulus		ASTMD790	11000	Mpa
Tensile modulus	23°C	ISO527-2	12600	Mpa
	Tensile modulus	100°C	ISO527-2	6830	Mpa
		Tensile modulus	150°C	ISO527-2	5310	Mpa
		Tensile modulus	Tensile modulus	175°C	ISO527-2	4830	Mpa
Tensile strength		ASTMD638	200	Mpa
Tensile stress	Break,23°C	ISO527-2	211	Mpa
	Tensile stress	Break,24°C	ISO527-2	125	Mpa
		Tensile stress	Break,150°C	ISO527-2	87.6	Mpa
		Tensile stress	Tensile stress	Break,175°C	ISO527-2	79.3	Mpa
elongation	Break	ASTMD638	2.5	%
Bending modulus	23°C	ISO178	10400	Mpa
	Bending modulus	100°C	ISO178	7170	Mpa
		Bending modulus	150°C	ISO178	4620	Mpa
		Bending modulus	Bending modulus	175°C	ISO178	4210	Mpa
bending strength		ASTMD790	290	Mpa
Bending stress	23°C	ISO178	296	Mpa
	Bending stress	100°C	ISO178	177	Mpa
		Bending stress	150°C	ISO178	111	Mpa
		Bending stress	Bending stress	175°C	ISO178	99.3	Mpa
compressive strength		ASTMD695	179	Mpa
shear strength		ASTMD732	89.6	Mpa
Poisson's ratio		7.58	0.41

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Annealed,3.20mm	ASTMD648	320	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	294	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTMD648	300	°C
Continuous use temperature 2		ASTMD3045	210	°C
Melting temperature		ISO11357-3	327	°C
Melting temperature	Melting temperature		ASTMD570	327	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	7.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.2E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTMD257	2E+16	ohms·cm
Dielectric strength	1.60mm	ASTMD149	20	KV/mm
Dielectric constant	60Hz	ASTMD150	3.80
Dielectric constant	Dielectric constant	1MHz	ASTMD150	3.60
Dissipation factor	60Hz	ASTMD150	4E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.012
Compared to the anti leakage trace index	CTI	UL746	600	V
High voltage arc tracing rate	HVTR	UL746	14.0	mm/min

Impact performance	Test Condition	Test Method	Test Result	Unit
Unscented Izod impact strength	23°C	ISO180/1U	59	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	67	kJ/m²

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance 4	1070nm:1.60mm	ASTMD1003	>20	%
Transmittance 4	Transmittance 4	940nm:1.60mm	ASTMD1003	>20	%

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating3	3.2mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.