Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA A-4133L BK324 SOLVAY USA
AMODEL®
Lawn and garden equipment、Electrical/Electronic App、Valves/valve components、Industrial components、Industrial applications、Thick wall accessories (c、Machine/mechanical compon、Metal substitution、Connector、Parts under the hood of a、Vehicle electronics、Application in the automo、Phone、currency、Shell
Chemical resistance、Low moisture absorption、Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
TD
ASTMD955
%
1
Water absorption rate
24hr
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
shear strength
ASTMD732
Mpa
8
Tensile strength
ASTMD638
Mpa
2
Tensile modulus
ASTMD638
Mpa
1
Tensile modulus
23°C
ISO527-2
Mpa
1
Tensile modulus
100°C
ISO527-2
Mpa
6
Tensile modulus
150°C
ISO527-2
Mpa
5
Tensile modulus
175°C
ISO527-2
Mpa
4
Tensile strain
断裂,23°C
ISO527-2
%
2
Tensile strain
断裂,24°C
ISO527-2
%
4
Tensile strain
断裂,150°C
ISO527-2
%
6
Tensile strain
断裂,175°C
ISO527-2
%
6
Tensile stress
断裂,23°C
ISO527-2
Mpa
2
Tensile stress
断裂,24°C
ISO527-2
Mpa
1
Tensile stress
断裂,150°C
ISO527-2
Mpa
8
Tensile stress
断裂,175°C
ISO527-2
Mpa
7
elongation
断裂
ASTMD638
%
2
Bending modulus
23°C
ISO178
Mpa
1
Bending modulus
100°C
ISO178
Mpa
7
Bending modulus
150°C
ISO178
Mpa
4
Bending modulus
175°C
ISO178
Mpa
4
Bending modulus
ASTMD790
Mpa
1
bending strength
ASTMD790
Mpa
2
Bending stress
23°C
ISO178
Mpa
2
Bending stress
100°C
ISO178
Mpa
1
Bending stress
150°C
ISO178
Mpa
1
Bending stress
175°C
ISO178
Mpa
9
compressive strength
ASTMD695
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
Continuous use temperature 2
ASTMD3045
°C
2
Hot deformation temperature
0.45MPa,Annealed,3.20mm
ASTMD648
°C
3
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
1.8MPa,退火,3.20mm
ASTMD648
°C
3
Melting temperature
ISO11357-3
°C
3
Melting temperature
ASTMD570
°C
3
Linear coefficient of thermal expansion
MD：0to100°C
ASTME831
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：100到200°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：0to100°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：100到200°C
ASTME831
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
High voltage arc tracing rate
HVTR
UL746
mm/min
1
Dielectric strength
1.60mm
ASTMD149
KV/mm
2
Volume resistivity
ASTMD257
ohms·cm
2
Compared to the anti leakage trace index
CTI
UL746
V
6
Impact performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
6
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
5
optical performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/A-4133L BK324
Transmittance 4
1070nm:1.60mm
ASTMD1003
%
>
Transmittance 4
940nm:1.60mm
ASTMD1003
%
>